Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 451 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	233 °C	451 °F	120°C/h; ISO 75/1
Polykemi AB SCANAMID 66 A12^ F25 NH10 Nylon 66, Glass Fiber Reinforced, Flame Retardant Information provided by Polykemi AB
Deflection Temperature at 1.8 MPa (264 psi)	233 Â°C	451 Â°F	ASTM D648
Kolon KOPAÂ® KN333HB30BL Hybrid Nylon 66 Hybrid, dimensionally stableApplications Timing belt coversInformation provided by API-Kolon.
Deflection Temperature at 1.8 MPa (264 psi)	233 Â°C @Thickness 3.20 mm	451 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP RFL46ES PA 66 LNP* LUBRICOMP* RFL46ES is a compound based on Nylon 6/6 containing 30% Glass Fiber, 20% PTFE. Added features of this grade include: Wear Resistant, Heat Stabilized, Easy Molding.
Deflection Temperature at 1.8 MPa (264 psi)	233 Â°C @Thickness 3.20 mm	451 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP RFP36 PA 66 LNP* LUBRICOMP* RFP36 is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE, Silicone. Added features of this material include: Wear Resistant.
Deflection Temperature at 1.8 MPa (264 psi)	233 Â°C @Thickness 3.20 mm	451 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP RFP36 PA 66 (Asia Pacific) LNP* Lubricomp* RFP36 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE, Silicone. Added features of this material include: Internally Lubricated. This product is also known as Lub..
Deflection Temperature at 1.8 MPa (264 psi)	233 Â°C @Thickness 3.20 mm	451 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP RFP36S PA 66 LNP* LUBRICOMP* RFP36S is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added features of this material include: Wear Resistant, Heat Stabilized.
Deflection Temperature at 1.8 MPa (264 psi)	233 Â°C @Thickness 3.20 mm	451 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP RFP36XXZ PA 66 (Asia Pacific) LNP Lubricomp RFP36XXZ is a compound based on Nylon 66 resin containing Glass Fiber, PTFE, Silicone. Added features of this material include: internally lubricated. Also known as Lubricomp RFL-4536 ..
Deflection Temperature at 1.8 MPa (264 psi)	233 Â°C @Thickness 3.20 mm	451 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP RX05495 PA 66 LNP LUBRICOMP* RX05495 is a compound based on Nylon 66 resin containing Glass Bead, Graphite, Glass Fiber. Added features of this material include: Easy Molding.
Deflection Temperature at 1.8 MPa (264 psi)	233 Â°C @Thickness 3.20 mm	451 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP RF0029S PA 66 LNP* THERMOCOMP* RF0029S is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added features of this material include: Flame Retardant, Heat Stabilized.
Deflection Temperature at 1.8 MPa (264 psi)	233 Â°C @Thickness 3.20 mm	451 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP RF0029S PA 66 (Asia Pacific) LNP* Thermocomp* RF0029S is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Heat Stabilized.
Deflection Temperature at 1.8 MPa (264 psi)	233 Â°C	451 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP RX08401 PA 66 LNP* Thermocomp* RX08401 is a compound based on Nylon 66 containing Glass Fiber. Added feature of this grade include: Impact Modified.
Deflection Temperature at 1.8 MPa (264 psi)	233 Â°C	451 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP RX96592 PA 66 LNP* Thermocomp* RX96592 is a compound based on Nylon 6/6 containing Proprietary Fillers.
Deflection Temperature at 1.8 MPa (264 psi)	233 Â°C	451 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP STAT-KON RE0029 PA 66 LNP* STAT-KON* RE0029 is a compound based on Nylon 66 resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant.
Deflection Temperature at 1.8 MPa (264 psi)	233 °C	451 °F	ASTM D648
Plenco 1508 Polyester, Briquette, Injection Molded PLENCO 01508 is a mineral filled pelletized polyester molding compound, which offers excellent heat resistance and electrical properties. UL recognized under component file E40654. 01508 is availabl..
Deflection Temperature at 1.8 MPa (264 psi)	233 °C	451 °F	ISO 75-1/-2
Unitika B2040G50 PA66, 50% Glass Fiber Reinforced, Dry Information provided by Unitika Ltd.
Deflection Temperature at 1.8 MPa (264 psi)	233 °C	451 °F	ASTM D648
Azdel AZMET® CM32350 35% continuous random fiber mat / PET resin matrix AZDEL® CM20350 is a glass mat thermoplastic laminate based upon a random oriented continuous fiber mat contained within a Polyethylene Terephthalate (PET) resin matrix. This composite material fea..
Deflection Temperature at 1.8 MPa (264 psi)	233 °C	451 °F	ASTM D648
DuPont Performance Polymers Rynite® 830ER NC010 PET Rynite® 830ER is 30% glass reinforced with excellent high temperature dielectric properties. Class H (180C).Information provided by DuPont Performance Polymers
Deflection Temperature at 1.8 MPa (264 psi)	233 °C	451 °F	Flatw 80x10x4, sp=64 mm; ISO 75/Af
Eurostar Star L PA66 15Y D52 PA66, Carbon Filled, Injection Molded Star L PA66 15Y D52 is a PTFE Lubricated, Carbon Fiber Reinforced, Polyamide 66 Injection Molding ResinInformation provided by Eurostar.