- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 417 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 417 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | ASTM Data |
| BASF Capron® SEG3 H1 15% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron SEG3 H1 is a 15% glass reinforced nylon 6 injection molding compound exhibiting. It exhibits exceptional surface aesthetics at the slower fill speeds associated with the gas assist injection .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | ASTM Data |
| BASF Capron® SEG6 H1 30% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron SEG6 H1 is a 30% glass reinforced nylon 6 injection molding compound. This material is currently under development as XA-2678. It exhibits exceptional surface aesthetics at the slower fill s.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C @Thickness 6.40 mm |
417 °F @Thickness 0.252 in |
ASTM D648 |
| Kingfa PA6-G50 50% Glass Fiber Reinforced PA6 Features:Good size stabilityLow tendency to wrapHigh mechanical propertiesGood low temperature resistanceGood surfaceExcellent balance propertiesApplications:Injection moldingAutomobile partsPower t.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C @Thickness 3.20 mm |
417 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP WFL34H PBT (Asia Pacific) LNP* LUBRICOMP* WFL34H is a compound based on Polybutylene Terephalate resin containing PTFE, Glass Fiber. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP WFL36 PBT (Asia Pacific) LNP LUBRICOMP* WFL36 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | Unannealed; ISO 75-2/A |
| Solvay Specialty Polymers Kalix® 2955 Polyamide, High Performance (HPPA), Glass Fiber Kalix® 2955 is a 27% bio-sourced, PA 6,10-based compound with 55% by weight glass fiber reinforcement. This material is specifically formulated for high strength and stiffness applications where .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | Unannealed; ISO 75-2/A |
| Solvay Specialty Polymers Lavanta® 5115 WH224 Polyester, High Performance (HPP), 15% Glass Fiber Lavanta® 5115 WH224 is a 15% glass fiber reinforced, high-performance polyester (HPP) injection molding grade developed specifically for HB LED packaging applications that utilize surface mount t.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON JX89626 PES LNP* STAT-KON* JX89626 is a compound based on Polyethersulfone containing Proprietary Fillers. Added feature of this material is: Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C @Thickness 3.20 mm |
417 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON JX89626 PES LNP* STAT-KON* JX89626 is a compound based on Polyethersulfone containing Proprietary Fillers. Added feature of this material is: Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP EC005 PEI (Europe-Africa-Middle East) LNP* THERMOCOMP* EC005 is a compound based on Polyetherimide resin containing Carbon Fiber. Added features include : Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP EC006 PEI (Europe-Africa-Middle East) LNP* THERMOCOMP* EC006 is a compound based on Polyetherimide resin containing Carbon Fiber. Added features include: Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP EC008 PEI (Europe-Africa-Middle East) LNP* THERMOCOMP* EC008 is a compound based on Polyetherimide resin containing Carbon Fiber. Added features include: Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP EX93452 PEI LNP THERMOCOMP* EX93452 is a compound based on Polyetherimide resin containing Proprietary Fillers. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C @Thickness 3.20 mm |
417 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP EX93452 PEI LNP THERMOCOMP* EX93452 is a compound based on Polyetherimide resin containing Proprietary Fillers. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C @Thickness 3.20 mm |
417 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP QF007 PA 6/10 LNP* THERMOCOMP* QF007 is a compound based on Nylon 6/10 resin containing 35% Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP QF008 PA6.10 LNP* THERMOCOMP* QF008 is a compound based on Nylon 6/10 resin containing 40% Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp QF008S PA 6/10 LNP* Thermocomp* QF008S is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Americas .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON EE004 PEI (Europe-Africa-Middle East) LNP* Stat-kon* EE004 is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Sax Polymers SAXAMID 126F10 Nylon 6, 50% Glass Fiber SAXAMID 126F10 is a polyamide 6 injection-molding-grade reinforced with 50% glass fibers.Information provided by SAX Polymers |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | ISO 75-1/-2 |
| Unitika A1022GFL60 PA6, 60% Glass Fiber Reinforced, Dry Information provided by Unitika Ltd. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | ISO 75-1, 2 |
| Polyplastics Duranex® 3400 Polybutylene Terephthalate (PBT), Standard, 40% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | ISO 75-1, 2 |
| Polyplastics Duranex® 3405 Polybutylene Terephthalate (PBT), Standard, 45% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | ISO 75 |
| BASF Ultramid® HMG13 HS BK-102 63% Glass Filled PA6 (Dry) Ultramid HMG13 HS BK-102 is a 63% glass filled, injection molding, high modulus nylon designed to have high strength and stiffness for metal replacement applications. It also has excellent moldabil.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 614 Nylon 6, Glass Reinforced Data provided by the manufacturer, ComAlloy International Company.45% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C @Thickness 3.18 mm |
417 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Solvay Specialty Polymers Veradel® AG-320 Polyethersulfone (PESU)
(Unverified Data**) Veradel AG-320 is a 20% glass fiber reinforced grade of polyethersulfone (PESU). Adding glass fiber to polyethersulfone substantially increases the rigidity, tensile strength, creep resistance, dime.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | Unannealed; ASTM D648 |
| LNP Lubricomp® QFL-4017 ER HS Polyamide 6/10 Copolymer, Glass Fiber Reinforcement, PTFE Lubricant
(discontinu Features: Heat Stabilized, Good Mold Release, LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C @Thickness 3.20 mm |
417 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP JF002 PES LNP THERMOCOMP* JF002 is a compound based on Polyethersulfone resin containing 10% Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp QF008S PA 6/10 (Asia Pacific) LNP* Thermocomp* QF008S is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Asia Paci.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | ASTM D648 |
| Plenco 51015 PET, Pellet, Injection Molded, White
(discontinued **) PLENCO 51015 is an engineering grade glass reinforced recycled polyethylene terephthalate resin designed for increased flexibility and good physical strength. It is UL listed.Information supplied by.. |
|||