Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 287 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 287 °C

@Thickness 3.20 mm
549 °F

@Thickness 0.126 in
Annealed; ASTM D648
Solvay Specialty Polymers Amodel® A-1145 HS Polyphthalamide (PPA), 45% Glass Fiber (Dry)
Amodel® A-1145 HS is a 45% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, very high flexural modulus and very high tensile strength. Excellent cr..
Deflection Temperature at 1.8 MPa (264 psi) 287 °C

@Thickness 3.20 mm
549 °F

@Thickness 0.126 in
Annealed; ASTM D648
Solvay Specialty Polymers Amodel® AS-1145 HS Polyphthalamide (PPA), 45% Glass Fiber (Dry)
Amodel® AS-1145 HS is a 45% glass reinforced heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater tha..
Deflection Temperature at 1.8 MPa (264 psi) 287 °C

@Thickness 3.20 mm
549 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP UF006H PPA
LNP* THERMOCOMP* UF006H is a compound based on Polyphthalamide resin containing 30% Glass Fiber. Added feature of this grade is: Healthcare.
Deflection Temperature at 1.8 MPa (264 psi) 287 °C

@Thickness 3.20 mm
549 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP UF006H PPA (Asia Pacific)
LNP* Thermocomp* UF006H is a compound based on Polyphthalamide resin containing Glass Fiber.
Deflection Temperature at 1.8 MPa (264 psi) 287 °C

@Thickness 3.18 mm
549 °F

@Thickness 0.125 in
Annealed; ASTM D648
Solvay Specialty Polymers Amodel® AS-1145 HS Polyphthalamide (PPA)  (Unverified Data**)
Amodel AS-1145 HS is a 45% glass reinforced heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater than 0...