Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 276 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	276 °C	529 °F	Annealed; ASTM D648
Solvay Specialty Polymers AvaSpire® AV-722 CF30 Polyaryletherketone (PAEK) (Unverified Data**) AvaSpire AV-722 CF30 is a 30% carbon fiber reinforced version of AvaSpire AV-722. This formulation offers improved part economics relative to 30% carbon fiber reinforced PEEK while retaining most of..
Deflection Temperature at 1.8 MPa (264 psi)	276 °C	529 °F	Annealed; ASTM D648
Solvay Specialty Polymers AvaSpire® AV-742 SL30 Polyaryletherketone (PAEK) (Unverified Data**) AV-742 SL30 is a wear resistant grade of AvaSpire polyaryletherketone (PAEK) designed to provide low wear rates in both non-lubricated and lubricated environments. In addition to outstanding wear re..
Deflection Temperature at 1.8 MPa (264 psi)	276 Â°C	529 Â°F	Unannealed; ISO 75-2/A
Solvay Specialty Polymers AmodelÂ® AT-6130 HS Polyphthalamide (PPA), 30% Glass Fiber (Dry) AmodelÂ® AT-6130 HS is a 30% glass-reinforced, toughened polyphthalamide (PPA) resin that has more elongation than other 30% glass-reinforced grades of AmodelÂ® resin. This grade was developed f..
Deflection Temperature at 1.8 MPa (264 psi)	276 Â°C	529 Â°F	Annealed; ASTM D648
Solvay Specialty Polymers AvaSpireÂ® AV-722 CF30 Polyaryletherketone (PAEK), 30% Carbon Fiber AvaSpireÂ® AV-722 CF30 is a 30% carbon fiber reinforced version of AvaSpireÂ® AV-722. This formulation offers improved part economics relative to 30% carbon fiber reinforced PEEK while retaining..
Deflection Temperature at 1.8 MPa (264 psi)	276 Â°C	529 Â°F	Annealed; ASTM D648
Solvay Specialty Polymers AvaSpireÂ® AV-742 SL30 Polyaryletherketone (PAEK) AV-742 SL30 is a wear resistant grade of AvaSpireÂ® polyaryletherketone (PAEK) designed to provide low wear rates in both non-lubricated and lubricated environments. In addition to outstanding wea..
Deflection Temperature at 1.8 MPa (264 psi)	276 Â°C	529 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP Thermocomp OC008A PPS - Branched LNP* Thermocomp* OC008A is a compound based on Branched Polyphenylene Sulfide containing Carbon Fiber.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 1.8 MPa (264 psi)	276 Â°C	529 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP Verton UV00A PPA LNP VERTON* UV00A is a compound based on Polyphthalamide resin containing Long Glass.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 1.8 MPa (264 psi)	276 Â°C	529 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP Verton UV00A PPA (Asia Pacific) LNP VERTON* UV00A is a compound based on Polyphthalamide resin containing Long Glass.This data was supplied by SABIC-IP for the Asia Pacific region.
Deflection Temperature at 1.8 MPa (264 psi)	276 °C	529 °F	Unannealed; ISO 75-2/A
Solvay Specialty Polymers Amodel® AT-6130 HS Polyphthalamide (PPA) (Unverified Data**) Amodel AT-6130 HS is a 30% glass-reinforced, toughened polyphthalamide (PPA) resin that has more elongation than other 30% glass-reinforced grades of Amodel resin. This grade was developed for autom..
Deflection Temperature at 1.8 MPa (264 psi)	276 °C	529 °F	As Molded; ASTM D648A
Sumitomo Bakelite North America RX® 647 Fiberglass Reinforced Phenolic RX 643 is a fiberglass reinforced, ammonia-free, phenolic resole compound, with good dimensional stability and good strength at elevated temperatures. Meets ASTM D-5948 Type GPI-10. RX 647 is a fibe..
Deflection Temperature at 1.8 MPa (264 psi)	276 °C	529 °F	ASTM D648
LATI LARAMID G/30 30% Glass Filled Polyphthalamide (PPA) Based Compound (Unverified Data**) Laramid compounds are based on a unique semi-crystalline engineering polymer (polyphthalamide) offering improved performance compared to traditional engineering thermoplastics at a lower cost than s..