Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 268 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 268 °C
514 °F
Unannealed; ASTM D648
LNP Thermocomp® OF-1006 Polyphenylene Sulfide, Glass Fiber Reinforcement  (discontinued **)
Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names..
Deflection Temperature at 1.8 MPa (264 psi) 268 °C

@Thickness 3.20 mm
514 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP OFL36 PPS - Branched (Asia Pacific)
LNP LUBRICOMP* OFL36 is a compound based on PPS - Branched resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Deflection Temperature at 1.8 MPa (264 psi) 268 °C

@Thickness 3.20 mm
514 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP OFL36A PPS - Branched (Europe-Africa-Middle East)
LNP LUBRICOMP* OFL36 is a compound based on PPS - Branched resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Deflection Temperature at 1.8 MPa (264 psi) 268 °C
514 °F
GB/T 1634.2-2004
Sichuan Deyang Haton® hGC51 PPS / AE Polyphenylene Sulfide
Injection molding, conductiveInformation provided by Sichuan Deyang Chemical Co., LTD
Deflection Temperature at 1.8 MPa (264 psi) 268 °C
514 °F
GB/T 1634.2-2004
Sichuan Deyang Haton® hGR30 Polyphenylene Sulfide, Glass Fiber Reinforced
Injection moldingInformation provided by Sichuan Deyang Chemical Co., LTD
Deflection Temperature at 1.8 MPa (264 psi) 268 °C
514 °F
GB/T 1634.2-2004
Sichuan Deyang Haton® hGR40 Polyphenylene Sulfide, Glass Fiber Reinforced
Injection moldingInformation provided by Sichuan Deyang Chemical Co., LTD
Deflection Temperature at 1.8 MPa (264 psi) 268 °C
514 °F
GB/T 1634.2-2004
Sichuan Deyang Haton® hGR40DL Polyphenylene Sulfide, Glass Fiber Reinforced
Injection molding, low chlorineInformation provided by Sichuan Deyang Chemical Co., LTD
Deflection Temperature at 1.8 MPa (264 psi) 268 °C
514 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP OCF62 PPS - Branched
LNP* THERMOCOMP* OCF62 is a compound based on PPS-Branched resin containing 10% Carbon Fiber, 30% Glass Fiber. Added feature of this material includes: Easy Molding
Deflection Temperature at 1.8 MPa (264 psi) 268 °C
514 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP OCF62E PPS - Branched
LNP* THERMOCOMP* OCF62E is a compound based on PPS-Branched resin containing 10% Carbon Fiber, 30% Glass Fiber. Added feature of this material includes: Easy Molding
Deflection Temperature at 1.8 MPa (264 psi) 268 °C
514 °F
ISO 75-1/-2
Barlog Plastics KEBAFLOW MX130 LCP, 30% glass fiber / mineral reinforced
LCP-GF/MD 30Information provided by BARLOG plastics GmbH.