Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 250 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	150 - 250 °C	302 - 482 °F	Average value: 180 °C Grade Count:32
Overview of materials for Phenolic, Novolac, Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Mineral Filled". Each property range of values reported is minimum and maximum values..
Deflection Temperature at 1.8 MPa (264 psi)	65.0 - 250 °C	149 - 482 °F	Average value: 122 °C Grade Count:64
Overview of materials for Nylon 6, 30% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Mineral Filled". Specific grades with primary filler content between 25% and 34% are includ..
Deflection Temperature at 1.8 MPa (264 psi)	200 - 250 °C	392 - 482 °F	Average value: 224 °C Grade Count:14
Overview of materials for Nylon 66/Nylon 6 Blend, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/Nylon 6 Blend, Glass Fiber Filled". Each property range of values reported is minimum and maxim..
Deflection Temperature at 1.8 MPa (264 psi)	61.0 - 250 °C	142 - 482 °F	Average value: 156 °C Grade Count:95
Overview of materials for Nylon 66, Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass Bead Filled". Each property range of values reported is minimum and maximum values of ap..
Deflection Temperature at 1.8 MPa (264 psi)	115 - 250 °C	239 - 482 °F	Average value: 181 °C Grade Count:9
Overview of materials for Nylon 66, 10% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 10% Mineral Filled". Specific grades with primary filler content between 5% and 14% are includ..
Deflection Temperature at 1.8 MPa (264 psi)	230 - 250 °C	446 - 482 °F	ISO 75 A
Vyncolit Vyntec® CF8030 Carbon Fiber Reinforced Novolac Phenolic Carbon fiber reinforced phenolic moldable composite with superior tribological properties. High tensile and flexural strength and modulus combined with low density.Information provided by Vyncolit,..
Deflection Temperature at 1.8 MPa (264 psi)	49.0 - 250 °C	120 - 482 °F	Average value: 144 °C Grade Count:231
Overview of materials for Nylon 6, Heat Stabilized This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Heat Stabilized". Each property range of values reported is minimum and maximum values of appro..