Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 375 °F | ASTM D648 |
Nylene® Vexel™ B12GF15 SA , 15% Glass Reinforced PBT Description: Vexel™ B12GF15 SA is a 15% glass fiber reinforced PBT with improved surface aPolyphenylene Etherarance. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 375 °F | ASTM D648 |
Oxford Polymers 15GF 15% Glass Fiber Reinforced Polybutylene Terephthalate (PBT) 15% Glass Fiber Reinforced Polybutylene Terephthalate (PBT)Information provided by Oxford Polymers. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 191 °C @Thickness 6.40 mm |
376 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP KONDUIT OX11314 PPS (Asia Pacific) Thermally conductive mineral filled PPS FR compound |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 376 °F | ASTM D648 |
Custom Resins Vexel™ 5100 RD PBT; 15% Glass Filled
(discontinued **) Improved Surface. Property data for dry as molded samples.Data provided by the manufacturer |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 191 °C @Thickness 3.20 mm |
376 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
SABIC Innovative Plastics LNP Stat-kon EE008E PEI LNP STAT-KON* EE008E is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Americas r.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 376 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP STAT-KON WEF32ISP PBT (Europe-Africa-Middle East) LNP * Stat-kon* WEF32ISP is a compound based on Polybutylene Terephalate resin containing Glass Fiber and Carbon Fiber. Added features include High Impact, Heat Stabilized and Electrically Conduct.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 191 °C @Thickness 3.20 mm |
376 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP THERMOCOMP WH0270B PBT LNP THERMOCOMP* WH0270B is a compound based on Polybutylene Terephalate resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 191 °C @Thickness 3.20 mm |
376 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP THERMOCOMP WH0270B PBT (Asia Pacific) LNP THERMOCOMP* WH0270B is a compound based on Polybutylene Terephalate resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 376 °F | ASTM D648 |
Sumitomo Bakelite Durez® 156 Phenolic, Compression Grade Durez 156 Black Phenolic is a two-stage, asbestos-free, heat resistant/electrical molding material. It exhibits excellent dimensional stability, high heat resistance, good molded appearance, and UL.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 375 °F | Unannealed; ASTM D648 |
Techmer ES HiFill® PBT GF15 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightInformation provided by TP Composites, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 375 °F | Unannealed; ASTM D648 |
Techmer ES Plastiblend® PA6 GF20 RM-B L NAT Nylon 6 Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightAdditive: LubricantFeatures: Low Moisture Absorption and LubricatedAppearance: BlackTPCI.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 376 °F | ASTM D648 |
Sumitomo Bakelite Durez® 29502 Phenolic, Compression Grade Durez 29502 Brown Phenolic is a two stage, asbestos free, glass filled, special purpose molding material. It is formulated for close tolerance applications such as transmission valve bodies, and di.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 376 °F | As Molded; ASTM D648A |
Sumitomo Bakelite North America FM 4005X4648 Fiberglass Reinforced Phenolic Novolac FM 4005X4648 a fiberglass reinforced phenolic novolac molding compound formulated to increase thermal conductivity and electrical conductance. This material also exhibits low post mold shrinkage.In.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 376 °F | ISO 75-1/-2 |
Unitika RUN35-C25 PA6, Dry High modulus and low warpage nylonInformation provided by Unitika Ltd. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 376 °F | ASTM D648 |
Plenco 4504 Phenolic, Granular, Compression Molded Plenco 04504 is a renumber of Plaslok 504. Plenco 04504 is a two-stage, mineral and cellulose-filled phenolic molding compound having better impact and heat resistance than general purpose molding c.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 376 °F | ASTM D648 |
A. Schulman ComAlloy Hiloy® 464 Glass Fiber/Bead Reinforced, PET Alloy Data provided by the manufacturer, ComAlloy International Company.25% Glass Fiber/Bead Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 375 °F | ASTM D648 |
Chase Plastics CP Pryme® N213GL (DAM) Nylon 6, 13% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 376 °F | ASTM D648 |
Plenco 4311 Phenolic, Granular, Transfer Molded PLENCO 04311 is a heat resistant, mineral filled phenolic molding compound offering excellent processability, mechanical strength, and improved cold powder pourability characteristics. UL recognized.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 376 °F | ASTM D648 |
Plenco 4485 Phenolic, Granular, Transfer Molded PLENCO 04485 is a mineral filled phenolic molding compound offering excellent heat resistance, electrical resistance, and dimensional stability. UL recognized under component file E40654. 04485 is a.. |