Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 183 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 183 °C
361 °F
120°C/h; ISO 75/1
Polykemi AB POLYshine PBT D234 GF30 FR PBT, Glass-Fiber Reinforced, Flame Retardant
Information provided by Polykemi AB
Deflection Temperature at 1.8 MPa (264 psi) 183 °C

@Thickness 6.40 mm
361 °F

@Thickness 0.252 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP KONDUIT PX10322 PA 6 (Asia Pacific)
Thermally conductive mineral filled PA6 FR compound, with through-plane and in-plane thermal conductivity of 1.7 W/(m*K) and 4.7 W/(m*K) respectively, conforming to ASTM E 1461 test standard.
Deflection Temperature at 1.8 MPa (264 psi) 183 °C
361 °F
ASTM D648
Gharda Chemicals Gafone S 1320GF Polysulfone (PS)  (discontinued **)
Characteristics: High Temperature Resistance - Tg 189°C Excellent Clarity Excellent Mechanical & Electrical properties Easy to process Very good Hydrolytic Resistance Applications: Elec..
Deflection Temperature at 1.8 MPa (264 psi) 183 °C
361 °F
ASTM D648
Plenco Valite 4224 Novolac Phenolic, Granular, Transfer Molded  (discontinued **)
This Valite product has been replaced by Plenco 4224. Data provided by Plenco.VALITE 4224 is a brown, two stage, general purpose phenolic molding compound. It has good electrical and moldability ch..
Deflection Temperature at 1.8 MPa (264 psi) 183 °C

@Thickness 3.20 mm
361 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP IFL21 PA6.12
LNP LUBRICOMP* IFL21 is a compound based on Nylon 6/12 resin containing 5% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant.
Deflection Temperature at 1.8 MPa (264 psi) 183 °C

@Thickness 3.20 mm
361 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics ULTEM ATX3562R PEI+PCE
50% Glass fiber and mineral filled, high flow Polyetherimide blend with internal mold release and enhanced dimensional stability. ECO Conforming.
Deflection Temperature at 1.8 MPa (264 psi) 183 °C

@Thickness 3.20 mm
361 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics ULTEM ATX3562R PEI+PCE (Asia Pacific)
50% Glass fiber and mineral filled, high flow Polyetherimide blend with internal mold release and enhanced dimensional stability. ECO Conforming.
Deflection Temperature at 1.8 MPa (264 psi) 183 °C

@Thickness 3.20 mm
361 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics ULTEM ATX3562R PEI+PCE (Europe-Africa-Middle East)
50% Glass fiber and mineral filled, high flow Polyetherimide blend with internal mold release and enhanced dimensional stability. RoHS compliant.
Deflection Temperature at 1.8 MPa (264 psi) 183 °C
362 °F
Unannealed; ASTM D648
Techmer ES HiFill® PSU GF10 10% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 10% Filler by WeightInformation provided by TP Composites, Inc.
Deflection Temperature at 1.8 MPa (264 psi) 183 °C

@Thickness 3.20 mm
361 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics LNP Thermocomp EB004 PEI
LNP* Thermocomp* EB004 is a compound based on Polyetherimide resin containing Glass Bead.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 1.8 MPa (264 psi) 183 °C

@Thickness 3.20 mm
361 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics LNP Thermocomp EB004 PEI (Asia Pacific)
LNP* Thermocomp* EB004 is a compound based on Polyetherimide resin containing Glass Bead.This data was supplied by SABIC-IP for the Asia Pacific region.
Deflection Temperature at 1.8 MPa (264 psi) 183 °C
361 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP Thermocomp QF002 PA6.10
LNP* Thermocomp* QF002 is a compound based on Nylon 6/10 containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 1.8 MPa (264 psi) 183 °C
361 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP Thermocomp WC003P Polyester Elastomer
LNP* Thermocomp* WC003P is a compound based on Polyester resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the A..
Deflection Temperature at 1.8 MPa (264 psi) 183 °C
361 °F
0.25 inch; ASTM D648
PlastxWorld CEVIAN® A5624 20% GF PA/ABS Alloy, DAM
Property data is for dry as molded (DAM) samples.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc.
Deflection Temperature at 1.8 MPa (264 psi) 183 °C
361 °F
ISO 75-1/-2
DSM Arnite® TV4 640 (PBT+PC) - GF20
20% Glass Reinforced
Deflection Temperature at 1.8 MPa (264 psi) 183 °C
361 °F
ISO 75
BASF Ultradur B 4300 G3 15% Glass Filled PBT
Ultradur B 4300 G3 is an easy flowing injection molding PBT with 15% glass fiber reinforcement for rigid, tough, and dimensionally stable parts.
Deflection Temperature at 1.8 MPa (264 psi) 183 °C
361 °F
ISO 75
BASF Ultrason S 2010 G4 20% Glass Filled PSU
Ultrason S 2010 G4 is a 20% glass reinforced, medium viscosity injection molding PSU grade with high rigidity and strength.
Deflection Temperature at 1.8 MPa (264 psi) 183 °C
361 °F
ASTM D648
A. Schulman ComAlloy E-16903B Nylon 6/6, Electrically Conductive - Stainless Steel Fiber Filled
Data provided by the manufacturer, ComAlloy International Company.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 1.8 MPa (264 psi) 183 °C
361 °F
ASTM D648
Plenco 7467 Phenolic, Nodular, Transfer Molded  (discontinued **)
Two-Stage Phenolic. PLENCO 07467 is an organic phenolic molding compound offering excellent dimensional stability under conditions of total water immersion. 07467 is formulated to provide improved ..