- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 155 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 155 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C @Thickness 3.18 mm |
155 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Geon™ Vinyl Packaging 2320 LCW Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C @Thickness 6.35 mm |
155 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| PolyOne Geon™ Vinyl Rigid Molding 87546 Polyvinyl Chloride, Rigid (PVC, Rigid) Provisional Data SheetInformation provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C @Thickness 3.18 mm |
155 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| PolyOne Geon™ Vinyl Rigid Molding MR840 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | ASTM D648 |
| RheTech Products FRP257-01 32% Talc Reinforced Polypropylene Copolymer, Flame Retardant, Black Applications: Electrical component housingsConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C @Thickness 3.18 mm |
155 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Nymax™ 1200 A Black 11 A Polyamide 66 (Nylon 66) The Nymax® 1200 Blend Series of nylon 6/6 materials are salt-and-pepper pelletized blends combining select nylon resins and process aids, performance modifiers, and color concentrates. These materi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C @Thickness 3.18 mm |
155 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Nymax™ 1200 A UV White 205 Polyamide 66 (Nylon 66) The Nymax® 1200 Blend Series of nylon 6/6 materials are salt-and-pepper pelletized blends combining select nylon resins and process aids, performance modifiers, and color concentrates. These materi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | ASTM D648 |
| RheTech Products HP532-01 20% Talc Reinforced High Performance Polypropylene, Non-UV Stabilized, Black Applications: Close out panelSpeaker grilleInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | ASTM D648 |
| RheTech Products T20P100-00 20% Talc Reinforced Polypropylene, Natural Applications: Electronic housingsConsolesIP componentsHVAC ducts - air distributionClose out panelDurable goodsInjection molding conditions reported in table.Information provided by RheTech Products.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | ASTM D648 |
| RheTech Products T20P100-248 20% Talc Reinforced Polypropylene, General Purpose Grey Applications: Durable goodsElectronics housingsHVAC ducts - air distributionInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | ASTM D648 |
| RheTech Products T20P100-517UV 20% Talc Reinforced Polypropylene, UV Stabilized, Interior DX9 Black Applications: Center consolesIP componentsClose out panelsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | ASTM D648 |
| Polymer Resources TP-FR2 Polybutylene Terephthalate, Flame Retardant Polybutylene Terephthalate, Flame Retardant Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | ASTM D648 |
| Polymer Resources TP-FR2-[color]-WR Polybutylene Terephthalate, Flame Retardant, Wear Resistant Polybutylene Terephthalate, Flame Retardant, Wear ResistantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Infor.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hylon® N1000STHL Nylon 6/6 (DAM) Information provided by Ravago |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hylon® N1000STL Nylon 6/6 (DAM)
(discontinued **) Information provided by Entec. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hylon® N1000STHL UV2 Nylon 6/6
(discontinued **) Available in North America Additive: Heat Stabilizer, Lubricant and UV StabilizerFeatures: Good Toughness, Lubricated, Heat StabilizedRoHS CompliantAuto Specifications: GM GMP.PA66.074 Color: BlackF.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | ASTM D648 |
| Spartech Royalite R86 PVC Acrylic Weather Resistant Sheet Description: Weather Resistant SheetInformation provided by Spartech. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | ASTM D648 |
| Spartech Royalstatâ„¢ R632 ABS/PVC Static Control Sheet Description: Static Control SheetInformation provided by Spartech. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | ASTM D648 |
| Spartech SP-3010 Rigid PVC Specialty Sheet Description: Specialty SheetInformation provided by Spartech. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill FR® PP FR-N X Availability: North AmericaForms: PelletsFeatures: Flame Retardant Appearance: Natural ColorInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | ASTM D648 |
| Plastics Group Polifil® 627L Nylon 6/6 (DAM) Polifil® NYLON 6/6 combines good abrasion and chemical resistance.Applications: ValvesBearingsBearing casesStandard processing techniques are applicable. Information provided by The Plastics Group... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1200 Calcium Carbonate-Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1200 is a 40% calcium carbonate-filled homopolymer polypropylene. Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1200 Calcium Carbonate-Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1200 is a 40% calcium carbonate-filled homopolymer polypropylene. Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1200 Calcium Carbonate-Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1200 is a 40% calcium carbonate-filled homopolymer polypropylene. Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | ASTM D648 |
| Asahi Kasei Thermofil P-20TC-5100R 20% Talc Filled, Heat Stabilized Information provided by Asahi Thermofil |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1200 Calcium Carbonate-Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1200 is a 40% calcium carbonate-filled homopolymer polypropylene. Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | ASTM D648 |
| RheTech Products M20P101-01 20% Mica Reinforced Polypropylene, Black Applications: Radiator air bafflesHVAC ductworkClose-out and filler panelsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | Unannealed (0.250"); ASTM D648 |
| LTL Color Compounds ColorFast® NY1 Nylon 6 Injection molding nylon 6, with or without lubeAll information provided by LTL Color Compounders, Inc. |
|||