Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 8.0 MPa 170 - 190 °C
338 - 374 °F
Injection; ISO 75-C
Raschig Group 3505 Epoxy
Glass-fiber reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. This product meets the allowed..
Deflection Temperature at 8.0 MPa 170 - 190 °C
338 - 374 °F
Injection; ISO 75-C
Raschig Group 3535 Epoxy
Glass fiber-reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties adn dimensional stability even at high temperatures. Form: Low dust granulate pack..
Deflection Temperature at 8.0 MPa 170 °C
338 °F
ISO 175
Perstorp Compounds Aminel GF Melamine
Fiberglass-reinforced melamine material with high dimensional stability, excellent injection properties and high thermal stabilityInformation provided by Perstorp Compounds Inc.
Deflection Temperature at 8.0 MPa 170 °C
338 °F
ISO 75-2
Hexion Bakelite™ PF 1107 Phenolic Formaldehyde Resin, Low Shrinkage, Resistant to High Temperatures  (disconti
Phenolic molding compound, inorganically filled, glass fiber reinforced, high heat resistance, low heat expansion coefficient, highest resistance to pressure, high dimensional stability.Application ..
Deflection Temperature at 8.0 MPa 170 °C
338 °F
ISO 75-2
Hexion Bakelite™ PF 6507 Phenolic Formaldehyde Resin, Elasticized, Low Shrinkage, Resistant to High Temperatures, High Mechanical Strength
Phenolic molding compound, inorganically filled, glass fiber reinforced, elastomer modified, galvanizable, heat resistant, good media resistance, high dimensional stability at raised temperature, hi..
Deflection Temperature at 8.0 MPa 170 °C
338 °F
ISO 75-1/-2
EMS-Grivory Grivory® 1SVX-65H black 9288 PA1010-GF65
Product Description: Grilamid 1SVX-65H black is a 65% glass fiber reinforced Polyamide 1010 injection molding grade with the following product profile: Raw materials based on renewable resources Exc..
Deflection Temperature at 8.0 MPa 170 °C
338 °F
ISO 75-1/-2
EMS-Grivory Grivory® 1SVX-65H nat PA1010-GF65
Product Description: Grilamid 1SVX-65H natural is a 65% glass fiber reinforced Polyamide 1010 injection molding grade with the following product profile: Raw materials based on renewable resources E..
Deflection Temperature at 8.0 MPa 170 °C
338 °F
ISO 75-1/-2
EMS-Grivory Grivory® GV-5HL black 9914 PA*-GF50
Product description: Grivory GV-5HL black 9914 is a 50% glass fiber reinforced engineering thermoplastic material based on a combination of semicrystalline polyamide with partially aromatic copolyam..
Deflection Temperature at 8.0 MPa 170 °C
338 °F
ISO 75-1/-2
EMS-Grivory Grivory® HT2V-3H LF PA*-GF30
Grivory TH2V-3H LF is a glass fiber reinforced (30%), PTFE modified engineering thermoplastic based on semi-crystalline partially aromatic copolyamide. Polymer designation acc. ISO: PA6T/66 Polymer ..
Deflection Temperature at 8.0 MPa 170 °C
338 °F
ISO 75-1/-2
EMS-Grivory Grivory® BG-50 H PA6-GF50
Product description: Grilon BG-50 H is a high heat stabilized PA6 injection molding grade with 50% glass fibers. Grilon BG-50 H has the following important properties: High stiffnessHigh heat resist..
Deflection Temperature at 8.0 MPa 170 °C
338 °F
ISO 75-1/-2
EMS-Grivory Grivory® BG-50 PA6-GF50
Product description: Grilon BG-50 is a heat stabilized, normal viscosity PA6 injection molding grade with 50% glass fibers. Grilon BG-50 has the following important properties: High stiffnessGood su..
Deflection Temperature at 8.0 MPa 170 °C
338 °F
ISO 75-1/-2
EMS-Grivory Grivory® BG-50 S PA6-GF50
Product description: Grilon BG-50 S is a heat stabilized PA6 injection molding grade with 50% glass fibers. Grilon BG-50 S has the following important properties: High stiffnessExcellent surface fin..
Deflection Temperature at 8.0 MPa 170 °C
338 °F
ISO 75-1/-2
EMS-Grivory Grivory® XE 4217 black 9233 PA6T/66-GF45
Product description: Grivory XE 4217 black 9233 is a high heat stabilized, 45% glass fiber reinforced, semicrystalline, thermoplastic engineering material for injection moulding. Polymer designation..
Deflection Temperature at 8.0 MPa 170 °C
338 °F
HDT/C; ISO 75-2
Akro-Plastic Akromid® B3 GF 40 (2474) PA 6 Dry, 40% Glass Filled
AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatur..
Deflection Temperature at 8.0 MPa 170 °C
338 °F
HDT/C; ISO 75-1/2
Akro-Plastic Akromid® S3 GF 50 1 (3533) PA 6.10 Dry, 50% Glass Filled
A characteristic property of AKROMID® S (PA 6.10) is that it has a renewable-resource content of up to 70 % and therefore fulfils the current definition of a bioplastic. The plant-based raw materia..
Deflection Temperature at 8.0 MPa >= 170 °C
>= 338 °F
ISO 75-C
Raschig Group DECAL® 152CL Phenolic
Glass-fiber and mineral reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This product meet..
Deflection Temperature at 8.0 MPa 170 °C
338 °F
ISO 75-2
Hexion Bakelite™ PF 6501 Phenolic Formaldehyde Resin, Low Shrinkage