Polymer Property : Deflection Temperature at 8.0 MPa = 140 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 8.0 MPa 140 - 160 °C
284 - 320 °F
ISO 75-C
Raschig Group DECAL® 666/8/2B Phenolic
Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This product meets the allowe..
Deflection Temperature at 8.0 MPa 140 °C
284 °F
HDT/C; ISO 75-1/2
Akro-Plastic Akromid® S3 GF 30 4 (3552) PA 6.10 Dry, 30% Glass Filled  (discontinued **)
A characteristic property of AKROMID® S (PA 6.10) is that it has a renewable-resource content of up to 70 % and therefore fulfils the current definition of a bioplastic. The plant-based raw materia..
Deflection Temperature at 8.0 MPa 140 °C
284 °F
ISO 75-1/-2
Lanxess Durethan® BCF 30 X H2.0 901510 Nylon 6, 30% Glass + Carbon Fiber
PA 6, injection molding grade, 30% reinforced (glass fibers + carbon fibers), conductive, intrinsic color black, good heat-ageing resistance
Deflection Temperature at 8.0 MPa 140 °C
284 °F
ISO 75-1/-2
Lanxess Durethan® BKV 35 HTS 901510 Nylon 6, 35% Glass Fiber
PA 6, injection molding grade, 35% glass fibers, very good heat-ageing resistance
Deflection Temperature at 8.0 MPa 140 °C
284 °F
ISO 75-1/-2
Lanxess Pocan® B 3225 000000 PBT, 20% Glass Fiber
PBT, 20% glass fibers, injection molding
Deflection Temperature at 8.0 MPa 140 °C
284 °F
ISO 75-1/-2
Lanxess Pocan® B 3225 901510 PBT, 20% Glass Fiber
PBT, 20% glass fibers, injection molding
Deflection Temperature at 8.0 MPa 140 - 160 °C
284 - 320 °F
ISO 75 C
Vyncolit 2923 W Novolac Phenolic
Mineral filled phenolic molding compound with excellent heat resistance and dimensional stability.Information provided by Vyncolit, a Sumitomo Bak Group
Deflection Temperature at 8.0 MPa 140 °C
284 °F
ISO 75-1/-2
EMS-Grivory Grivory® HT XE 3996 PA*-GF30
Product description: Grivory XE 3996 black 9225 is a 30% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. ISO-Polymer designatio..
Deflection Temperature at 8.0 MPa 140 °C
284 °F
ISO 75-1/-2
EMS-Grivory Grivory® HTV-3H1 nat PA6T/6I-GF30
Product description: Grivory HTV-3H1 natural is a 30% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Acc. to ISO: PA 6T/6I. Ac..
Deflection Temperature at 8.0 MPa 140 °C
284 °F
ISO 75-1/-2
EMS-Grivory Grivory® LV-65H FWA black 9225 PA12-GF65
Product description: Grilamid LV-65H FWA black 9225 is a 65 % glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: High stiffness combine..
Deflection Temperature at 8.0 MPa 140 °C
284 °F
ISO 75-1/-2
EMS-Grivory Grivory® LV-65H FWA nat PA12-GF65
Product description: Grilamid LV-65H FWA natural is a 65 % glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: High stiffness combined w..
Deflection Temperature at 8.0 MPa 140 °C
284 °F
ISO 75-1/-2
EMS-Grivory Grivory® XE 4104 nat PA610-GF40
Product description: Grilamid XE 4104 natural is a 40% glass fiber reinforced, heat stabilized polyamide 610 injection molding grade. This product is to a large extent based on renewable raw materia..
Deflection Temperature at 8.0 MPa 140 °C
284 °F
ISO 75-1/-2
EMS-Grivory Grivory® XE 4164 black 9225 PA*-GF30
Product description: Grivory XE 4164 black 9225 is a 30% glass fiber reinforced engineering thermoplastic material based on a semicrystalline, partially aromatic copolyamide. ISO polymer designation..
Deflection Temperature at 8.0 MPa 140 °C
284 °F
ISO 75-1/-2
EMS-Grivory Grivory® BG-50 HM PA6-GF50
Product description: Grilon BG-50 HM is a heat stabilized, normal viscosity, and adhesion modified PA6 injection molding grade with 50% glass fibers. Grilon BG-50 HM has the following important prop..
Deflection Temperature at 8.0 MPa 140 °C
284 °F
ISO 75-1/-2
EMS-Grivory Grivory® BGK-30 X PA6-(GF+GB)30
Information provided by EMS Grivory
Deflection Temperature at 8.0 MPa 140 °C
284 °F
ISO 75-1/-2
EMS-Grivory Grivory® HT1V-3 FWA nat PA6T/6I-GF30
Product description: Grivory HT1V-3 FWA natural is a 30 wt.-% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Acc. to ISO: PA 6..