Polymer Property : Deflection Temperature at 8.0 MPa = 120 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 8.0 MPa 100 - 120 °C
212 - 248 °F
Injection; ISO 75-C
Raschig Group 2567 AMC
Glass fiber-reinforced and inorganically filled polyester molding compound (UP) in various colors. Outstanding mechanical strength similar to BMC/SMC, very good electrical isolation properties and ..
Deflection Temperature at 8.0 MPa 100 - 120 °C
212 - 248 °F
Injection; ISO 75-C
Raschig Group 3536 Epoxy
Glass-fiber reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. This product meets the allowed..
Deflection Temperature at 8.0 MPa 100 - 120 °C
212 - 248 °F
ISO 75-C
Raschig Group DECAL® 2061 Phenolic
Wood flour reinforced phenolic molding compound. Good electrical properties, chemical resistance and mechanical properties. This product meets the allowed upper limits for heavy metals and PCAs and ..
Deflection Temperature at 8.0 MPa 100 - 120 °C
212 - 248 °F
ISO 75-C
Raschig Group DECAL® 5431 Phenolic
Organically and inorganically filled phenolic molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/..
Deflection Temperature at 8.0 MPa 80.0 - 120 °C
176 - 248 °F
ISO 75-C
Raschig Group RALUPOL® 2100 UP Polyester
Organically and inorganically filled polyester molding compound. Low post-shrinkage, very good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy meta..
Deflection Temperature at 8.0 MPa 70.0 - 120 °C
158 - 248 °F
Injection; ISO 75-C
Raschig Group RALUPOL® 2200 UP Polyester
Organically filled polyester molding compound. Low post-shrinkage, good electrical values and mechanical properties, high surface quality and good color stability (non-yellowing). This product meets..
Deflection Temperature at 8.0 MPa 100 - 120 °C
212 - 248 °F
ISO 75-C
Raschig Group 3572 Epoxy
Glass-fiber reinforced epoxy molding compound. Good mechanical strength and electrical strength, enhanced elasticity for ensuring good sealing under extreme heat and/or humidity, good chemical resis..