- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 66.0 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 66.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | Compression Molded; ASTM D648 |
| NOVA Chemicals Surpass® RMs244-UG Octene sHDPE Rotational Molding Film Features: Octene copolymerExceptional low temperature propertiesOutstanding stiffnessBroad processing windowSuperior whiteness for improved part appearanceEasy mold releaseNSF listed for Standards 1.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | ASTM D648 |
| Eastman 7352 PET
(discontinued **) VORIDIAN PET thermoplastic polyesters are condensation polymers produced by a continuous melt-phase polymerization process followed by a solid-state polymerization process. VORIDIAN PET polyester 73.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | |
| Spartech Spectrum® S370 TPO Polyolefin Sheet
(discontinued **) Data provided by the manufacturer. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | Compression Molded; ASTM D648 |
| NOVA Chemicals Surpass® RMs244-U Octene sHDPE Rotational Molding Film Features: Octene copolymerExceptional low temperature propertiesOutstanding stiffnessBroad processing windowSuperior whiteness for improved part appearanceEasy mold releaseNSF listed for Standards 1.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | Method A; ASTM D648 |
| Chevron Phillips Marlex® C513UV HDPE Blow Molding Resin
(discontinued **) Resin Type: Hexene CopolymerCharacteristics: Outstanding impact resistanceExcellent ESCRExcellent processabilityUV stabilizationApplications: Intermediate bulk containersAgricultural containersInfor.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | ASTM D648 |
| LyondellBasell Petrothene® LP5002 High Density Polyethylene (Blow Molding Grade) ApplicationsThe PETROTHENE LP series of polyethylene resins exhibits excellent environmental stress crack resistance and is especially designed for bottles containing aggressive agricultural and hou.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | ASTM D648 |
| LyondellBasell Petrothene® LP500200 High Density Polyethylene (Sheet & Profile Grade) ApplicationsThe PETROTHENE LP 5002 series of polyethylene resins exhibits excellent environmental stress crack resistance.Regulatory StatusThe LP 5002 base resin meets the requirements of Food and D.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | ASTM D648 |
| LyondellBasell Petrothene® LP500210 High Density Polyethylene (Sheet & Profile Grade) ApplicationsThe PETROTHENE LP 5002 series of polyethylene resins exhibits excellent environmental stress crack resistance.Regulatory StatusThe LP 5002 base resin meets the requirements of Food and D.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | ISO 75 |
| LyondellBasell Hifaxâ„¢ ETA-3104HF Thermoplastic Olefin Resin Key Features: medium melt flow, medium modulus thermoplastic elastomeric olefin resin, good impact and stiffness balance, good dimensional stability, good processabilityApplications: molded-in color.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C @Thickness 3.20 mm |
151 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66 LNP LUBRILOY* R2000A is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C @Thickness 3.20 mm |
151 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66 (Asia Pacific) LNP LUBRILOY* R2000A is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C @Thickness 3.20 mm |
151 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66 (Europe-Africa-Middle East) LNP LUBRILOY* R2000A is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | ISO 75-2 |
| Borealis Borclear™ RE936CF Polypropylene Random Copolymer Borclear™ RE936CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. Applications: food packaging, lamination films, and stationary fil.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | ISO 75-2 |
| Borealis Bormed™ RE806CF Polypropylene Random Copolymer Bormed™ RE806CF is a random copolymer. The material is specially formulated for medical applications. Applications: Bormed™ RE806CF is recommended for medical packaging. Bormed™ RE806CF contai.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | ASTM D648 |
| Eastman Eastar EN052 Polyester Eastar Polyester EN052 is a thermoplastic condensation homopolymer produced by a continuous melt-phase polymerization process followed by a solid-state polymerization process. It has been crystalliz.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | ASTM D648 |
| Eastman Eastar EN067 Copolyester, Natural Eastar Copolyester EN067 is a copolymer PET with good color. This product is supplied as a crystalline pellet that has improved flowability characteristics. Due to slower crystallization kinetics, t.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | ASTM D648 |
| Eastman Eastar MN052 Polyester, Natural Eastar polyester MN052 is a thermoplastic condensation homopolymer produced by a continuous melt-phase polymerization process followed by a solid-state polymerization process. It has been crystalliz.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | ASTM D648 |
| Chevron Phillips Marlex® C513UV High Density Polyethylene, Blow Molding This extra high molecular weight, hexane copolymer is tailored for intermediate bulk container applications that require:Outstanding impact resistanceOutstanding ESCRExcellent processabilityUV stabi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | ASTM-D648 |
| Braskem AD57 HDPE Monofilament Polyethylene Copolymer AD57 resin is a high-density polyethylene, copolymer of butene-1, produced by the solution process, designed for raffia extrusion, and Raschel knitted with excellent optical and mechanical propertie.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | ASTM D648 |
| Arkema Group Pebax® 5533 Polyether Block Amide (PEBA) Information provided by Arkema Group |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | |
| Arkema Group Pebax® 5533 SN 01 Polyether Block Amide (PEBA) (Conditioned) POLYETHER BLOCK AMIDE(PEBA) hardness 55 shore D Non plasticized flexible Polyamide Outstanding mechanical properties at low temperature (-40°C) Applications: overmolded parts for sport good (Footba.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 - 90.6 °C | 151 - 195 °F | Average value: 77.3 °C Grade Count:18 |
| Overview of materials for PVC, Molded This property data is a summary of similar materials in the MatWeb database for the category "PVC, Molded". Each property range of values reported is minimum and maximum values of appropriate MatWeb.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | ASTM D648 |
| ExxonMobil Paxon™ AG45-004 Blow Molding Resin
(discontinued **) AG45-004 is a blow molding high density polyethylene which offers exceptional stress crack resistance and impact performance. It contains an antistat which permits this resin to be used in all food.. |
|||