Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 62.0 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C
144 °F
ASTM D 648
NOVA Chemicals Surpass® RMs341-U Octene sHDPE Rotational Molding Resin
RMs341-U complies with the U.S. FDA regulations for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food. RMs341-..
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C
144 °F
ISO 75-1/-2
DuPont Performance Polymers Hytrel® HTR8685 BK022A TPC-ET  (Unverified Data**)
Hytrel® HTR8685 BK022A is designed for blow molding or processing techniques requiring high melt viscosity. It has nominal hardness of 44D, is pigmented black with fine particle size carbon black,..
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C
144 °F
ASTM D 648
NOVA Chemicals Surpass® RMs341-UG Octene sHDPE Rotational Molding Resin
RMs341-UG complies with the U.S. FDA regulations for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food. RMs341..
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C

@Thickness 4.00 mm
144 °F

@Thickness 0.157 in
after annealing 150°C 16 hr; ASTM D648
Solvay Specialty Polymers Solef® 21508 PVDF Copolymer  (discontinued **)
Key features of this grade: High Elongation, Wire & Cable, Plenum, Formulated. Recommended processing is extrusion. Available as powder & granules.General information about SOLEF® PVDF: SOLEF® P..
Deflection Temperature at 0.46 MPa (66 psi) 62.0 - 82.0 °C
144 - 180 °F
Average value: 74.6 °C Grade Count:12
Overview of materials for Styrene-Butadiene Copolymer, SBC
This property data is a summary of similar materials in the MatWeb database for the category "Styrene-Butadiene Copolymer, SBC". Each property range of values reported is minimum and maximum values ..
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C
144 °F
ASTM D648
LyondellBasell Alathon® L5332CP High Density Polyethylene
ApplicationsALATHON L 5332CP, formerly known as LYHD 048, is designed to meet the requirements of AAHTO M294 stress crack resistance. It exhibits excellent processing stability and high crush resis..
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C
144 °F
ASTM D648
LyondellBasell Alathon® L5332CP High Density Polyethylene, Blow Molding Grade
ALATHON L5332CP is bimodal molecular weight distribution, fractional melt index HDPE resin that exhibits an exceptional balance of environmental stress crack resistance and stiffness. Typical applic..
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C
144 °F
ASTM D648-97
Ipiranga Petrochem MB 0310 MDPE
IPQ employs Spherilene technology from Basell in the production of MDPE. The raw materials, which are supplied by COPESUL, are pre-treated and fed into gas-phase reactors, where medium density polye..
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C
144 °F
ASTM D648
LyondellBasell Hifaxâ„¢ ETA-3131EUV Thermoplastic Olefin Resin
Key Features: fractional melt flow, medium modulus, UV-stabilized, extrusion grade thermoplastic olefin resin, excellent impact and stiffness balance, good practical impact, good processability, exc..
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C
144 °F
ISO 75
Styrolution Styrolux 3G55 SBC
Styrolux 3G55 is a thermoplastic styrene-butadiene block copolymer which is suitable for film and sheet extrusion, and thermoforming. It offers and outstanding combination of crystal clarity and ex..
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C
144 °F
ASTM D648
SK Chemicals SKYPEL P147D Productivity Grade
SKYPEL is a thermoplastic polyester elastomer (TPEE). It is a polymer resin having the property somewhere between plastics and rubber, which have various properties ranging from high hardness plasti..
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C

@Thickness 3.20 mm
144 °F

@Thickness 0.126 in
ISO 75
A. Schulman FORMION™ FI 555-31 Recycled Ionomer
Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C

@Thickness 3.20 mm
144 °F

@Thickness 0.126 in
ISO 75
A. Schulman FORMION™ FI 555-31 Recycled Ionomer
Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C

@Thickness 3.20 mm
144 °F

@Thickness 0.126 in
ISO 75
A. Schulman FORMION™ FI 555-31 Recycled Ionomer
Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C

@Thickness 3.20 mm
144 °F

@Thickness 0.126 in
ISO 75
A. Schulman FORMION™ FI 555-31 Recycled Ionomer
Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C

@Thickness 3.20 mm
144 °F

@Thickness 0.126 in
ISO 75
A. Schulman FORMION™ FI 555-31 Recycled Ionomer
Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C

@Thickness 3.20 mm
144 °F

@Thickness 0.126 in
ISO 75
A. Schulman FORMION™ FI 555-31 Recycled Ionomer
Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C
144 °F
Method A; ASTM D-648
Chevron Phillips Marlex® HMN TR-938/938G Polyethylene; MDPE
Medium density polyethylene. These hexene copolymers are tailored for rotational molding applications that require: Wide process windows and good flowLong-term UV stabilizationExcellent impact stre..
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C
144 °F
dry; ISO 75-1/-2
DSM Novamid® ST145 NAT PA6-I
Impact Modified, Injection Molding
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C
144 °F
ASTM D648
ExxonMobil LL 8460.29 Rotational Molding Resin
Product Description: LL 8460 is a linear low density hexene copolymer designed to offer excellent ESCR and toughness. This resin is ideally suited for applications that require the optimum balance o..
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C
144 °F
ASTM D648
ExxonMobil LLP8460.29 Rotational Molding Resin
Product Description: LL 8460 is a linear low density hexene copolymer designed to offer excellent ESCR and toughness. This resin is ideally suited for applications that require the optimum balance o..
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C
144 °F
0.125";; ASTM D648
Diamond Polymers NPP11-0242 Polyethylene
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C
144 °F
ASTM D648
3D Systems Accura® Xtreme Plastic for SLA® Systems
For use with solid-state stereolithography (SLA®) systemsApplicationsForm, fit and function prototypesDurable AssembliesSnap fit assembliesTough enclosuresConsumer electronic componentsMaster patte..
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C
144 °F
BASF Novolen® 2900 H Polypropylene
Injection molded and thermoformed parts.Data was collected by ISO methods and provided by BASF.
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C

@Thickness 4.00 mm
144 °F

@Thickness 0.157 in
after annealing 150°C 16 hr; ASTM D648
Solvay Specialty Polymers Solef® 20810 PVDF Copolymer  (discontinued **)
Key features of this grade: Li Battery, Virgin. Recommended processing is solution. Available as powder & granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorinated semi-crysta..
Deflection Temperature at 0.46 MPa (66 psi) 62.0 - 143 °C
144 - 290 °F
Average value: 85.9 °C Grade Count:19
Overview of materials for High Density Polyethylene (HDPE), Extruded
This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Extruded". Each property range of values reported is minimum and maxim..
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C
144 °F
ASTM D648
ExxonMobil LL 8460 Rotational Molding Resin  (discontinued **)
LL 8460 is a linear low density hexene copolymer designed to offer excellent ESCR and toughness. This resin is ideally suited for applications that require optimum balance of stiffness, processabili..
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C
144 °F
ASTM D648
Formosa Plastics Formolene® L64220U Rotational Molding LLDPE  (discontinued **)
Linear Low Density Polyethylene Hexene Copolymer for Rotational Molding Formolene® L64220U is a general-purpose rotational molding linear low density resin made using the BP Gas Phase ProcessTM. Th..