Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 567 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 297 °C

@Thickness 3.18 mm
567 °F

@Thickness 0.125 in
Annealed; ASTM D648
Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA)  (Unverified Data**)
Amodel AS-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater than 0..
Deflection Temperature at 0.46 MPa (66 psi) 297 °C

@Thickness 3.20 mm
567 °F

@Thickness 0.126 in
Annealed; ASTM D648
Solvay Specialty Polymers Amodel® AE-1133 Polyphthalamide (PPA), 33% Glass Fiber
Amodel® AE-1133 is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) designed to work in the modern automotive electrical environment. It has a high heat deflection temperature, high ..
Deflection Temperature at 0.46 MPa (66 psi) 297 °C

@Thickness 3.20 mm
567 °F

@Thickness 0.126 in
Annealed; ASTM D648
Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry)
Amodel® AS-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater th..
Deflection Temperature at 0.46 MPa (66 psi) 297 °C

@Thickness 3.20 mm
567 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP 4X08423 FP-P (PFA)
LNP* THERMOCOMP* 4X08423 is a compound based on PFA resin containing Glass Fiber.
Deflection Temperature at 0.46 MPa (66 psi) 297 °C

@Thickness 3.20 mm
567 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP UF00ASW PPA
LNP* Thermocomp* UF00ASW is a compound based on Polyphthalamide (PPA) containing glass fiber. Characteristics of this grade of Heat Stabilized and Hot Water Moldable.
Deflection Temperature at 0.46 MPa (66 psi) 297 °C

@Thickness 3.20 mm
567 °F

@Thickness 0.126 in
Annealed; ASTM D648
Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry)
Amodel® A-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, high flexural modulus and high tensile strength. Excellent creep resist..
Deflection Temperature at 0.46 MPa (66 psi) 297 °C
567 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP Verton UV00ASXS PPA (Europe-Africa-Middle East)
LNP* VERTON* UV00ASXS is a compound based on Polyphthalamide resin containing Long Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Deflection Temperature at 0.46 MPa (66 psi) 297 °C
567 °F
ASTM Test
BASF Ultramid® 1703-2 BK ND3007 25% Glass Filled PA66 (Dry)
Ultramid 1703-2 BK ND3007 is a 25% glass reinforced, heat stabilized injection molding nylon 6/6.
Deflection Temperature at 0.46 MPa (66 psi) 297 °C
567 °F
ASTM Test
BASF Ultramid® 1503-2 BK ND3007 33% Glass Filled PA66 (Dry)
Ultramid 1503-2 BK ND3007 is a 33% glass reinforced, heat stabilized, pigmented black injection molding PA6/6.
Deflection Temperature at 0.46 MPa (66 psi) 297 °C
567 °F
ASTM Test
BASF Ultramid® 1503-2 NF2004 33% Glass Filled PA66 (Dry)
Ultramid 1503-2 NF2004 is a 33% glass reinforced, heat stabilized injection molding PA6/6.