Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 538 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 281 °C
538 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP THERMOCOMP OCF62 PPS - Branched
LNP* THERMOCOMP* OCF62 is a compound based on PPS-Branched resin containing 10% Carbon Fiber, 30% Glass Fiber. Added feature of this material includes: Easy Molding
Deflection Temperature at 0.46 MPa (66 psi) 281 °C
538 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP THERMOCOMP OCF62E PPS - Branched
LNP* THERMOCOMP* OCF62E is a compound based on PPS-Branched resin containing 10% Carbon Fiber, 30% Glass Fiber. Added feature of this material includes: Easy Molding
Deflection Temperature at 0.46 MPa (66 psi) 281 °C

@Thickness 3.20 mm
538 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP VERTON UF-700-12 HS EXP PPA (Asia Pacific)
LNP* Verton* UF-700-12 HS EXP is a compound based on Polyphthalamide resin containing Long Glass Fiber. Added features of this material include: Heat Stabilized.
Deflection Temperature at 0.46 MPa (66 psi) 281 °C
538 °F
ASTM D648
A. Schulman ComAlloy® E-13819 Heat Dissipative PPS
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 0.46 MPa (66 psi) 281 °C
538 °F
ASTM D648
A. Schulman ComAlloy® E-13819 Heat Dissipative PPS
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 0.46 MPa (66 psi) 281 °C
538 °F
ASTM D648
A. Schulman ComAlloy® E-13819 Heat Dissipative PPS
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 0.46 MPa (66 psi) 281 °C
538 °F
ASTM D648
A. Schulman ComAlloy® E-13819 Heat Dissipative PPS
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 0.46 MPa (66 psi) 281 °C
538 °F
ASTM D648
A. Schulman ComAlloy® E-13819 Heat Dissipative PPS
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 0.46 MPa (66 psi) 281 °C
538 °F
ASTM D648
A. Schulman ComAlloy® E-13819 Heat Dissipative PPS
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 0.46 MPa (66 psi) 281 °C

@Thickness 3.20 mm
538 °F

@Thickness 0.126 in
Unannealed; ASTM D648
LNP Verton™ UF-700-12 Polyphthalamide, Long Glass Fiber Filled  (discontinued **)
LNP™ Verton™ UF-700-12 HS EXP is a compound based on Polyphthalamide resin containing Long Glass Fiber. Added features of this material include: Heat Stabilized.Information provided by LNPThis dat..