Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C @Thickness 3.20 mm |
487 °F @Thickness 0.126 in |
ASTM D648 |
Ovation Polymers Opnyl OP66GF43 Nylon 66, As Conditioned Nylon 66-Glass reinforced(43%), high tensile strength, stiffness and HDT.Information provided by Ovation Polymers |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | Unannealed; ASTM D648 |
LNP Thermocomp® FP-EC-1004 Ethylene Tetrafluoroethylene Copolymer, Carbon Fiber Reinforcement
(discontinued * Features: Electrically ConductiveForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C @Thickness 6.40 mm |
487 °F @Thickness 0.252 in |
ASTM D648 |
Kingfa PA66-G15 15% Glass Fiber Reinforced PA66 Features:Good size stabilityLow tendency to wrapHigh mechanical propertiesGood low temperature resistanceGood surfaceExcellent balance propertiesApplications:Injection moldingAutomobile partsPower t.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics LNP LUBRICOMP RFL369 PA6.6 (Europe-Africa-Middle East) LNP* LUBRICOMP* RFL369 is a compound based on PA 66 resin containing Glass Fiber, PTFE, Flame Retardant. Added features include: Flame Retardant, internally lubricated |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C @Thickness 3.20 mm |
487 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP LUBRILOY UA200A PPA LNP LUBRILOY* UA200A is a compound based on Polyphthalamide resin containing Aramid Fiber, Proprietary Lubricant. Added feature of this material is: Wear Resistant. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C @Thickness 3.20 mm |
487 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP LUBRILOY UA200A PPA (Asia Pacific) LNP LUBRILOY* UA200A is a compound based on Polyphthalamide resin containing Aramid Fiber, Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics LNP THERMOCOMP RF0049SP PA 66 LNP* THERMOCOMP* RF0049SP is a compound based on Nylon 66 containing 20% Glass Fiber. Added features of this grade include: Flame Retardant, Heat Stabilized. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics LNP Thermocomp RF004S PA 66 LNP* Thermocomp* RF004S is a Nylon 6/6 containing Glass Fiber. Characteristics are Heat Stabilized.This data was supplied by SABIC-IP for the Americas region. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics LNP THERMOCOMP RFB53XXZ PA 66 LNP* THERMOCOMP* RFB53XXZ is a compound based on Nylon 66 resin containing 15% Glass Fiber, 25% Glass Bead. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C @Thickness 3.20 mm |
487 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP THERMOCOMP RX12402 PA 66 LNP* Thermocomp* RX12402 is a compound based on PA66 containing 60% Glass Fiber. Added feature is Superior Flow. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics LNP THERMOCOMP RX96592 PA 66 LNP* Thermocomp* RX96592 is a compound based on Nylon 6/6 containing Proprietary Fillers. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics LNP STAT-KON RE0029 PA 66 LNP* STAT-KON* RE0029 is a compound based on Nylon 66 resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics LNP Thermocomp RFB53U PA 66 (Europe-Africa-Middle East) LNP*THERMOCOMP*RFB53U is a compound based on PA 66 resin containing Glass Bead, Glass Fiber. Added features include: UV-Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle E.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics LNP THERMOCOMP RX99732C PA 66 LNP* Thermocomp* PDX-R-99732 is a Nylon 6/6 with proprietary fillers. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C @Thickness 3.20 mm |
487 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP THERMOTUF VF006U Super Tough Nylon LNP* Thermotuf* VF006U is a compound based on Super Tough Nylon containing Glass Fiber. Characteristics of this grade are High Impact. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | ASTM D648 |
A. Schulman SCHULAMID® 66 GF33 33% Glass Fiber Reinforced Nylon 66 Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | ASTM D648 |
A. Schulman SCHULAMID® 66 GF33H 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | ASTM D648 |
A. Schulman SCHULAMID® 66 GF33 33% Glass Fiber Reinforced Nylon 66 Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | ASTM D648 |
A. Schulman SCHULAMID® 66 GF33H 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | ASTM D648 |
A. Schulman SCHULAMID® 66 GF33 33% Glass Fiber Reinforced Nylon 66 Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | ASTM D648 |
A. Schulman SCHULAMID® 66 GF33H 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | ASTM D648 |
A. Schulman SCHULAMID® 66 GF33H 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | ASTM D648 |
A. Schulman SCHULAMID® 66 GF33 33% Glass Fiber Reinforced Nylon 66 Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | ASTM D648 |
A. Schulman SCHULAMID® 66 GF33H 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | ASTM D648 |
A. Schulman SCHULAMID® 66 GF33H 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | ASTM D648 |
A. Schulman SCHULAMID® 66 GF33 33% Glass Fiber Reinforced Nylon 66 Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
Eurostar Staramide RFB53U PA66, 50% Glass Bead/Fiber Filled, Injection Molded RFB53U is a Glass Bead/ Glass Fiber Reinforced Polyamide 66 Injection Molding Resin (also known as Staramide 66 1525 VK Z4)Information provided by Eurostar. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | ASTM D648 |
A. Schulman ComAlloy Lubrilon® 620 Nylon 6/6, Glass Fiber/Molybdenum Disulfide Filled, Flow Enhanced Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | ASTM D648 |
A. Schulman ComAlloy Lubrilon® 628 Nylon 6/6, Glass Fiber/Molybdenum Disulfide Filled, Flow Enhanced Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics LNP VERTON RV00CEXS PA 66 LNP* VERTON* RV00CEXS is a compound based on Nylon 66 resin containing 60% Long Glass Fiber. Added features of this grade include: Easy Molding, Structural. |