Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 412 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 211 °C

@Thickness 6.35 mm
412 °F

@Thickness 0.250 in
Unannealed; ASTM D648
PolyOne LubriOne™ CTX-502 Natural Polyether Imide (PEI)
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
Deflection Temperature at 0.46 MPa (66 psi) 211 °C
412 °F
ASTM D648
Polymer Resources PEI-G30 Polyetherimide, 30% Glass Reinforced
Polyetherimide, 30% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Poly..
Deflection Temperature at 0.46 MPa (66 psi) 211 °C
412 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP LUBRICOMP EX06405 PEI
LNP* LUBRICOMP* EX06405 is a compound based on Polyetherimide resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractible, Easy Molding.
Deflection Temperature at 0.46 MPa (66 psi) 211 °C
412 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP LUBRICOMP EX06405 PEI (Asia Pacific)
LNP* Lubricomp* EX06405 is a compound based on Polyetherimide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
Deflection Temperature at 0.46 MPa (66 psi) 211 °C
412 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP LUBRICOMP IFL36L PA6.12
LNP* LUBRICOMP* IFL36L is a compound based on Nylon 6/12 containing 30% Glass Fiber, 15% PTFE. Added features of this grade include: Low Extractable, Wear Resistant.
Deflection Temperature at 0.46 MPa (66 psi) 211 °C

@Thickness 3.20 mm
412 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics Ultem 1010RF PEI
Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming. US FDA and EU Food Contact Compliant in recognized colors.This data was supplied by SABIC-IP for the Americas reg..
Deflection Temperature at 0.46 MPa (66 psi) 211 °C

@Thickness 3.20 mm
412 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics Ultem 2412EPR PEI
40% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.This data was supplied by SABIC-IP for the Am..
Deflection Temperature at 0.46 MPa (66 psi) 211 °C

@Thickness 3.20 mm
412 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics Ultem 2412EPR PEI (Asia Pacific)
40% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.This data was supplied by SABIC-IP for the As..
Deflection Temperature at 0.46 MPa (66 psi) 211 °C

@Thickness 3.20 mm
412 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics Ultem 2412EPR PEI (Europe-Africa-Middle East)
40% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.This data was supplied by SABIC-IP for the Eu..
Deflection Temperature at 0.46 MPa (66 psi) 211 °C

@Thickness 3.20 mm
412 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics LNP Stat-kon EE006EM PEI
LNP* Stat-kon* EE006EM is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding.This data was supplied by ..
Deflection Temperature at 0.46 MPa (66 psi) 211 °C

@Thickness 3.20 mm
412 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics LNP Stat-kon EE006EM PEI (Asia Pacific)
LNP* Stat-kon* EE006EM is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding.This data was supplied by ..
Deflection Temperature at 0.46 MPa (66 psi) 211 °C

@Thickness 3.20 mm
412 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics LNP Thermocomp EF008E PEI
LNP* Thermocomp* EF008E is a compound based on Polyetherimide resin containing Glass Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Americas..
Deflection Temperature at 0.46 MPa (66 psi) 211 °C

@Thickness 3.20 mm
412 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics LNP Thermocomp EF008E PEI (Asia Pacific)
LNP* Thermocomp* EF008E is a compound based on Polyetherimide resin containing Glass Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Asia Pac..
Deflection Temperature at 0.46 MPa (66 psi) 211 °C

@Thickness 3.20 mm
412 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics ULTEM JD7201 PEI (Asia Pacific)
Deflection Temperature at 0.46 MPa (66 psi) 211 °C
412 °F
ASTM D648
A. Schulman SCHULAMID® 6 GF15H 15% Glass Bead Reinforced, Heat Stabilized Nylon 6
Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 211 °C
412 °F
ASTM D648
A. Schulman SCHULAMID® 6 GF15H 15% Glass Bead Reinforced, Heat Stabilized Nylon 6
Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 211 °C
412 °F
ASTM D648
A. Schulman SCHULAMID® 6 GF15H 15% Glass Bead Reinforced, Heat Stabilized Nylon 6
Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 211 °C
412 °F
ASTM D648
A. Schulman SCHULAMID® 6 GF15H 15% Glass Bead Reinforced, Heat Stabilized Nylon 6
Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 211 °C
412 °F
ASTM D648
A. Schulman SCHULAMID® 6 GF15H 15% Glass Bead Reinforced, Heat Stabilized Nylon 6
Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 211 °C
412 °F
ASTM D648
A. Schulman SCHULAMID® 6 GF15H 15% Glass Bead Reinforced, Heat Stabilized Nylon 6
Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 211 °C
412 °F
ISO 75
BASF Ultramid® 8262G HS BK-102 7/13% Glass/Mineral Filled PA6 (Dry)
Ultramid 8262G HS BK-102 is a heat stabilized, pigmented black, 20% glass and mineral reinforced PA6 injection molding compound resulting in a balance of engineering properties with excellent dimens..
Deflection Temperature at 0.46 MPa (66 psi) 211 °C
412 °F
ASTM Test
BASF Ultramid® TG3S BK-104 15% Glass Filled PA6 (Dry)
Ultramid TG3S BK-104 is a 15% glass reinforced, heat stabilized, impact modified PA6 injection molding compound developed for applications requiring improved toughness in combination with a balance ..
Deflection Temperature at 0.46 MPa (66 psi) 211 °C
412 °F
ISO 75
BASF Ultramid® TG3S BK-104 15% Glass Filled PA6 (Dry)
Ultramid TG3S BK-104 is a 15% glass reinforced, heat stabilized, impact modified PA6 injection molding compound developed for applications requiring improved toughness in combination with a balance ..
Deflection Temperature at 0.46 MPa (66 psi) 211 °C
412 °F
ASTM D648
Polymer Resources PEI-G30 Polyetherimide, 30% Glass Reinforced  (Unverified Data**)
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.