- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 330 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 330 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | ASTM D648 |
| Polymer Resources AH-GP1 Acetal Homopolymer, Low Flow, High Melt Strength, Heat Stabilized Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | ASTM D648 |
| Polymer Resources AH-GP3 Acetal Homopolymer, High Flow Resin, Heat Stabilized Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | ASTM D648 |
| Polymer Resources NY6-M40 Nylon 6, 40% Mineral Filled Nylon 6, 40% Mineral Filled, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | ASTM D648 |
| Polymer Resources NY6-M40-[color]-H Nylon 6, 40% Mineral Filled, Heat Stabilized Nylon 6, 40% Mineral Filled, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon g.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | ASTM D648 |
| Polymer Resources AH-GP3 Acetal Homopolymer, High Flow Resin
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6 IM 435 HS L Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impact Modified and LubricatedUses: Low Temperature ApplicationsInformatio.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6 IM 511 HS L Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impact Modified and LubricatedUses: Low Temperature ApplicationsInformatio.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6 IM 835 HS L Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impact Modified and LubricatedProcessing Method: Injection MoldingInformat.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6 IM HS L BK Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impact Modified and LubricatedUL File Number: E157318Processing Method: In.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6 IM L Availability: North AmericaForms: PelletsAdditive: Impact Modifier and LubricantFeatures: Impact Modified and LubricatedInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6 IM L W Availability: North AmericaForms: PelletsAdditive: Impact Modifier and LubricantFeatures: Impact Modified and LubricatedProcessing Method: Injection MoldingInformation provided by TP Composites, Inc.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6 IM X Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impact Modified and LubricatedProcessing Method: Injection MoldingInformat.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® POM CO GF20 TL15 20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 20% Filler by WeightAdditive: PTFE Lubricant(15%)Features: Lubricated, Copolymer, Good Wear Resistance and Low FrictionInf.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® POM CO TL2 MB Acetal Availability: North AmericaForms: PelletsAdditive: PTFE Lubricant(2%)Features: Lubricated, Good Wear Resistance, Low Friction and CopolymerInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® POM CO TS20 Acetal Availability: North AmericaForms: PelletsAdditive: PTFE Lubricant(20%) and Silicone LubricantFeatures: Lubricated, Good Wear Resistance and CopolymerInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® POM HO TL2 Acetal Availability: North AmericaForms: PelletsAdditive: PTFE Lubricant(2%)Features: Lubricated, Good Wear Resistance and HomopolymerInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | Unannealed; ASTM D648 |
| Techmer ES Plastiblend® PA6/ABS 1120 B1 Availability: North AmericaForms: PelletsAdditive: Impact ModifierFeatures: Impact ModifiedUL File Number: E157318Information provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | Unannealed; ASTM D648 |
| Techmer ES Electrablend® PA6 IM A Nylon 6 Availability: North AmericaForms: PelletsAdditive: Lubricant, Impact Modifier and Heat StabilizerFeatures: Conductive, Impact Modified, Heat Stabilized and LubricatedAppearance: BlackInformation pro.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | Unannealed; ASTM D648 |
| Chase Plastics CP Pryme® AC125 Acetal Copolymer, 25% Glass Fiber Reinforced Features: Glass fiber reinforcedAlkali resistantGood chemical resistanceGood dimensional stabilityFatigue resistantLow frictionGrease resistantLow moisture absorptionOil resistantResilientHigh rigid.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C @Thickness 3.17 mm |
330 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Chase Plastics CP Pryme® AH100 Acetal Homopolymer Information provided by Chase Plastics. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | ASTM D648 |
| Asahi Kasei Thermylene® P6-40FB-Y947 40% Glass Fiber/Glass Bead, Heat Stabilized Information provided by Asahi Thermofil |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | ASTM D648 |
| Asahi Kasei Thermylene® P7-40FG-0600 40% Glass Fiber Reinforced, Heat Stabilized Information provided by Asahi Thermofil |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | Unannealed, 0.125 in bars; ASTM D648 |
| PolyOne Edgetek® AT-25GF-10MN/000 BLASCK Acetal-Copolymer, Glass/Mineral Filled
(discontinued **) Description/Features:Glass/Mineral ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | Unannealed, 0.125 in bars; ASTM D648 |
| PolyOne Edgetek® AT-25GF-10MN/000 NATURAL Acetal-Copolymer, Glass/Mineral Filled
(discontinued **) Description/Features:Glass/Mineral ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | ASTM D648 |
| Polymer Resources AH-GP2 Acetal Homopolymer, Medium Flow, General Purpose Molding
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® POM CO GF20 TL20 20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 20% Filler by WeightAdditive: PTFE LubricantFeatures: Lubricated and CopolymerInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | ASTM D648 |
| Quantum Acetal-Homopolymer Information provided by Quantum Advanced Engineering Plastics |
|||