 POLYMER SEARCH

Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 264 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 264 °C
507 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP KONDUIT OTF2B PPS - Linear
LNP KONDUIT* OTF2B is a compound based on PPS - Linear resin containing 10% Glass Fiber, 55% Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Deflection Temperature at 0.46 MPa (66 psi) 264 °C
507 °F
Unannealed; ISO 75B-1, -2
LNP Konduit® OTF-212-11 Polyphenylene Sulfide, Proprietary Filler  (discontinued **)
Features: Thermally ConductiveForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades ar..
Deflection Temperature at 0.46 MPa (66 psi) 264 °C

@Thickness 3.20 mm
507 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP RX00713H PA 66
LNP* Thermocomp* RX00713H is a compound based on Nylon 6/6 containing proprietary fillers. Characteristics of this grade are: Healthcare.
Deflection Temperature at 0.46 MPa (66 psi) 264 °C
507 °F
ISO 75
BASF Ultramid® 1503-2 BK ND3007 33% Glass Filled PA66 (Dry)
Ultramid 1503-2 BK ND3007 is a 33% glass reinforced, heat stabilized, pigmented black injection molding PA6/6.
Deflection Temperature at 0.46 MPa (66 psi) 264 °C
507 °F
ISO 75
BASF Ultramid® 1503-2 NF2004 33% Glass Filled PA66 (Dry)
Ultramid 1503-2 NF2004 is a 33% glass reinforced, heat stabilized injection molding PA6/6.
Deflection Temperature at 0.46 MPa (66 psi) 264 °C
507 °F
ISO 75
BASF Ultramid® 1503-2F BK ND 3007 33% Glass Filled PA 66 (Dry)
Description: Ultramid 1503-2F BK ND3007 is a 33% glass reinforced, heat stabilized injection molding PA6/6 grade. It is designed to provide enhance hydroysis resistance for under-the-hood applicatio..
Deflection Temperature at 0.46 MPa (66 psi) 264 °C
507 °F
Unannealed; ISO 75B-1, -2
LNP Konduit® OTF-212-11 BK8-115 Polyphenylene Sulfide, Proprietary Filler  (discontinued **)
Features: Thermally ConductiveForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades ar..
Deflection Temperature at 0.46 MPa (66 psi) 264 °C
507 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP VERTON RVN17SXS PA 66 (Europe-Africa-Middle East)
LNP* VERTON* RVN17SXS is a compound based on PA 66 resin containing Long Glass Fiber, MoS2. Added features include; Wear Resistant.
Deflection Temperature at 0.46 MPa (66 psi) 264 °C
507 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP VERTON RX970079 PA 66 (Europe-Africa-Middle East)
LNP* VERTON* RX970079 is a compound based on PA 66 resin containing Long Glass Fiber and PTFE. Added features include; Internally Lubricated.
Deflection Temperature at 0.46 MPa (66 psi) 264 °C
507 °F
ISO 75
BASF Ultramid® 1603-2 NF2004 43% Glass Filled PA66 (Dry)
Ultramid 1603-2 NF2004 is a 43% glass reinforced, heat stabilized injection molding nylon 6/6 with the highest level of glass reinforcement for maximum strength and stiffness.