Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 263 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 263 °C

@Thickness 3.20 mm
505 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics EXTEM UH1006 TPI Blend (Asia Pacific)
High heat amorphous TPI Blend, Chemical Resistant
Deflection Temperature at 0.46 MPa (66 psi) 263 °C

@Thickness 3.20 mm
505 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics EXTEM UH1006 TPI Blend (Europe-Africa-Middle East)
High heat amorphous TPI Blend, Chemical Resistant
Deflection Temperature at 0.46 MPa (66 psi) 263 °C

@Thickness 3.20 mm
505 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics EXTEM UH1006M TPI Blend (Europe-Africa-Middle East)
High heat amorphous TPI Blend, Chemical Resistant
Deflection Temperature at 0.46 MPa (66 psi) 263 °C

@Thickness 3.20 mm
505 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics EXTEM UH1016 TPI Blend
High heat amorphous TPI Blend, Chemical Resistant, High Flow
Deflection Temperature at 0.46 MPa (66 psi) 263 °C

@Thickness 3.20 mm
505 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics EXTEM UH1016 TPI Blend (Asia Pacific)
High heat amorphous TPI Blend, Chemical Resistant, High Flow
Deflection Temperature at 0.46 MPa (66 psi) 263 °C

@Thickness 3.20 mm
505 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics EXTEM UH1016 TPI Blend (Europe-Africa-Middle East)
High heat amorphous TPI Blend, Chemical Resistant, High Flow
Deflection Temperature at 0.46 MPa (66 psi) 263 °C

@Thickness 3.20 mm
505 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics Extem UH1016M TPI Blend
High heat amorphous TPI Blend, Chemical ResistantThis data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
Unannealed; ASTM Data
Dow Questra® EA503 High Heat Syndiotactic Polystyrene, 30% Glass Filled  (discontinued **)
QUESTRA® Crystalline Polymers are semi-crystalline engineering thermoplastic resins produced from styrene monomer using a proprietary metallocene catalyst system. These syndiotactic polymers are ve..
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
Unannealed; ASTM Data
Dow Questra® EA513 High Heat Syndiotactic Polystyrene, 30% Glass Filled  (discontinued **)
QUESTRA® Crystalline Polymers are semi-crystalline engineering thermoplastic resins produced from styrene monomer using a proprietary metallocene catalyst system. These syndiotactic polymers are ve..
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
Unannealed; ASTM Data
Dow Questra® QA805 High Heat Syndiotactic Polystyrene, 30% Glass Filled  (discontinued **)
QUESTRA® Crystalline Polymers are semi-crystalline engineering thermoplastic resins produced from styrene monomer using a proprietary metallocene catalyst system. These syndiotactic polymers are ve..
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
Unannealed; ASTM Data
Dow Questra® WA205 High Heat Syndiotactic Polystyrene, 30% Glass Filled  (discontinued **)
QUESTRA® Crystalline Polymers are semi-crystalline engineering thermoplastic resins produced from styrene monomer using a proprietary metallocene catalyst system. These syndiotactic polymers are ve..
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
Unannealed; ASTM Data
Dow Questra® WA206 High Heat Syndiotactic Polystyrene, 40% Glass Filled  (discontinued **)
QUESTRA® Crystalline Polymers are semi-crystalline engineering thermoplastic resins produced from styrene monomer using a proprietary metallocene catalyst system. These syndiotactic polymers are ve..
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
Unannealed; ASTM Data
Dow Questra® WA207 High Heat Syndiotactic Polystyrene, 30% Glass Filled  (discontinued **)
QUESTRA® Crystalline Polymers are semi-crystalline engineering thermoplastic resins produced from styrene monomer using a proprietary metallocene catalyst system. These syndiotactic polymers are ve..
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
Unannealed; ASTM Data
Dow Questra® WA551 High Heat Syndiotactic Polystyrene, 40% Glass Filled  (discontinued **)
QUESTRA® Crystalline Polymers are semi-crystalline engineering thermoplastic resins produced from styrene monomer using a proprietary metallocene catalyst system. These syndiotactic polymers are ve..
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
Unannealed; ASTM Data
Dow Questra® WA552 High Heat Syndiotactic Polystyrene, 30% Glass Filled  (discontinued **)
QUESTRA® Crystalline Polymers are semi-crystalline engineering thermoplastic resins produced from styrene monomer using a proprietary metallocene catalyst system. These syndiotactic polymers are ve..
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
ISO 75/Bf
Solvay TECHNYL® A 218W V33 Natural T PA66, 33% glass fiber, DRY
Description: TECHNYL® A 218W V33 Nat T is a polyamide 66, reinforced with 33% of glass fiber, heat stabilized, for injection molding. This product is available in natural color.Benefits: The prod..
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
ASTM D648
Techmer ES Electrafil® J-1/CF/30 Nylon 66, 30% Carbon Fiber Reinforced
Carbon Fiber Reinforced
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
Unannealed; ASTM D648
Techmer ES HiFill® PA6/6 GF33 33% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: LubricantFeatures: LubricatedTPCI# 8682101Information provided by TP Composite..
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
Unannealed; ASTM D648
Techmer ES HiFill® PA6/6 GF33 L UV 33% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Lubricant and UV StabilizerFeatures: Lubricated and Good UV ResistanceTPCI# 82..
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
Unannealed; ASTM D648
Techmer ES Luriblend® PA6/6 GF43 ML2 BK 43% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 43% Filler by WeightAdditive: Molybdenum Disulfide Lubricant(2%)Features: Lubricated Appearance: BlackTPCI# 8047101Informa..
Deflection Temperature at 0.46 MPa (66 psi) 263 °C

@Thickness 3.20 mm
505 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP STAT-KON RE007 PA 66
LNP* STAT-KON* RE007 is a compound based on PA66 resin containing 35% Carbon Fiber. Added features include: Electrically Conductive.
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP VERTON RV007SX9 PA 66 (Europe-Africa-Middle East)
LNP* VERTON* RV007SX9 is a compound based on PA 66 resin containing Long Glass Fiber.
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
ASTM D648
A. Schulman ComAlloy® E-14292 Hi-Flow Glass Reinforced PPS
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
ASTM D648
A. Schulman ComAlloy® E-14292 Hi-Flow Glass Reinforced PPS
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
ASTM D648
A. Schulman ComAlloy® E-14292 Hi-Flow Glass Reinforced PPS
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
ASTM D648
A. Schulman ComAlloy® E-14292 Hi-Flow Glass Reinforced PPS
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
ASTM D648
A. Schulman ComAlloy® E-14292 Hi-Flow Glass Reinforced PPS
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
DAM; ISO 75-1/-2
DuPont Performance Polymers Zytel® PLUS PLS95G35DH1 BK031 Nylon
Zytel® PLS95G35DH1 BK031is a high flow 35% glass reinforced PA using SHIELD Technology, only from DuPont, combining excellent surface appearance, excellent welding and fatigue retention, exceptiona..
Deflection Temperature at 0.46 MPa (66 psi) 263 °C
505 °F
ASTM D648
A. Schulman ComAlloy E-16822-1B Internally Lubricated, Carbon Fiber Reinforced Nylon 6/6
Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma..
Deflection Temperature at 0.46 MPa (66 psi) 263 °C

@Thickness 3.20 mm
505 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP STAT-KON OE002 PPS - LINEAR
LNP* STAT-KON* OE002 is a compound based on PPS - Linear resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive.