- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 220 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 220 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | ASTM D648 |
| RheTech Products FRP300-01 20% Talc Reinforced Polypropylene Copolymer, Flame Retardant, Black Applications: Electrical component housingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | ASTM D648 |
| RheTech Products T10P250-01 10% Talc Reinforced Polypropylene Copolymer, General Purpose Black Applications: Wire troughFan shroudsElectrical housingsUnderhood componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | ASTM D648 |
| RheTech Products T20P250-00 20% Talc Reinforced Polypropylene Copolymer, Non-UV Stabilized, Natural Applications: Air ductsHush panelsWire troughBracketsDurable goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | ASTM D648 |
| RheTech Products T20P250-699UV 20% Talc Reinforced Polypropylene Copolymer, UV Stabilized, AC20157-120 Black Applications: Window trimCowl screensExterior componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | ASTM D648 |
| RheTech Products T20P250-731UV 20% Talc Reinforced Polypropylene Copolymer, UV Stabilized, AS20698 Black Applications: Automotive trimIP componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | ASTM D648 |
| Polymer Resources PPX-SF1 Modified-PPO, Structural Foam Grade, Flame Retardant, Easy Flow Modified-Polyphenylene Oxide, Structural Foam Grade, Easy FlowFeatures: • Flame Retardant • Bromine Free • Chlorine Free • Self ExtinguishingProcess: Foam MoldingNotes: All physical, mechani.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | ASTM D648 |
| Polymer Resources PPX-SF2 Modified-PPO, Structural Foam Grade, Flame Retardant Modified-Polyphenylene Oxide, Structural Foam Grade, Standard FlowFeatures: • Flame Retardant • Bromine Free • Chlorine Free • Self ExtinguishingProcess: Foam MoldingNotes: All physical, mec.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | ASTM D648 |
| Polymer Resources ABS-G15 ABS, 15% Glass Reinforced Acrylonitrile Butadiene Styrene, 15% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 - 116 °C | 220 - 240 °F | Average value: 109 °C Grade Count:4 |
| Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Glass Fiber Filled, Flame Retardant". Each property range of valu.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hylac® FR134G10 ABS, 10% Glass Fiber Reinforced Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Rava.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | ASTM D648 |
| LTL Color Compounds ColorRxâ„¢ PP1-2002AF Food Grade Polypropylene Homopolymer A 20 melt injection molding grade of Polypropylene homopolymer with FDA food contact approval and antimicrobial protection.All information provided by LTL Color Compounders, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | ASTM D648 |
| LTL Color Compounds ColorRxâ„¢ PP1-2005ARX Biocompatible Polypropylene Homopolymer A biocompatible 20 melt injection molding grade of Polypropylene homopolymer for healthcare applications, containing a high level of antimicrobial protection for FDA regulated medical devices.All in.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® HIPS GF15 15% Glass Filled Availability: North AmericaForms: PelletsGlass Fiber Reinforcement, 15% Filler by WeightInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® HIPS GF30 30% Glass Filled Availability: North AmericaForms: PelletsGlass Fiber Reinforcement, 30% Filler by WeightAppearance: BlackInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | ASTM D648 |
| Techmer ES Electrafil® J-1200/CF/10 ABS, 10% Carbon Fiber Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill FR® PP CO FR-N Availability: North AmericaForms: PelletsFeatures: Flame Retardant, High Impact Resistance and CopolymerInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | ASTM D648 |
| Plastics Group Polifil® GFABS-20 20% Glass-Reinforced Acrylonitrile-Butadiene Styrene (ABS) Polifil® GFABS series compounds combine the most desirable properties of both components - allowing for enhanced processability and toughness together with the stiffness of glass.Applications: Fire.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | Unannealed; ASTM D648 |
| Chase Plastics CP Pryme® A110 ABS, 10% Glass Fiber Reinforced Features: Glass fiber reinforcementInjection moldingForm: PelletsInformation provided by Chase Plastics. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | ASTM D648 |
| Washington Penn Homopolymer Polypropylene 40% Calcium Carbonate Filled Calcium carbonate-filled polypropylene compounds have been tailored specifically to meet the requirements of each of the major automobile producers. Grades are available to meet FDA food and drug pa.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | unannealed; molded and tested in accordance with ASTM D 4101; ASTM D648 |
| Dow 5D49 Polypropylene Resin DOW 5D49 is intended for use fiber spinning processes. It is well suited for spunbond non-woven applications.Information provided by DowDow Announced Sale of Global Polypropylene Business to Braske.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | unannealed; molded and tested in accordance with ASTM D 4101; ASTM D648 |
| Dow 5E89 Polypropylene Resin DOW 5E89 is intended for use in stretched tape (raffia) processes, from which the raffia is used to produce woven fabrics for carpet backing, sacking, industrial and geotextile applications.Informat.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | ASTM D648 |
| Aaron Industries AAROLENE® ARPP 200-2 PP Black Polypropylene Copolymer AAROLENE® ARPP 200 Series Polypropylene Compounded ResinFeatures: A high flow polypropylene copolymer resin, pre-colored black, specifically designed for all high speed injection molding applicati.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | ASTM D648 |
| Aaron Industries AAROPRENE® CFIPP 2020 High Impact Calcium Carbonate Filled Polypropylene AAROPRENE® CFIPP 2000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | ASTM D648 |
| Aaron Industries AAROPRENE® CFPP 2030 Calcium Carbonate Filled Polypropylene AAROPRENE® CFPP 2000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | ASTM D648 |
| Spartech EP6120 Filled and Reinforced Copolymer Filled copolymers offer a higher level of impact performance than homopolymer materials, and higher stiffness than unfilled copolymers. Copolymer based materials retain much of their impact strength.. |
|||