- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 202 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 202 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 395 °F | ASTM D648 |
| Polymer Resources NY66-IM2-LM Nylon, Preliminary Data Sheet, Low Flexural Modulus, High Impact (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 395 °F | ASTM D648 |
| Polymer Resources TP-FRHG30 Polybutylene Terephthalate, 30% Glass Reinforced Alloy, Flame Retardant Polybutylene Terephthalate, 30% Glass Reinforced Alloy, Flame RetardantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test s.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 396 °F | ASTM D648 |
| Shell Carilon® DP R1000 Polyketone
(discontinued **) Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON® Thermoplastic Polymer DP R1000 is a high flow developmental engineering polyketone resin from Shell Chemi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C @Thickness 3.20 mm |
396 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Lubricomp EFP36G PEI LNP* EFP36G is a Polyetherimide base resin containing a Mixed Glass Fiber and PTFE/Silicone.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 396 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Ultem 2212 PEI (Europe-Africa-Middle East) 20% Milled glass filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 396 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics ULTEM 2212R PEI (Europe-Africa-Middle East) 20% Milled glass filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. Resin is RoHS compliant. UL94 V0 and 5VA listing. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C @Thickness 3.20 mm |
396 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP WI001 PBT LNP* LUBRICOMP* WI001 is a compound based on PBT containing 2% Silicone. Added feature of this grade is: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C @Thickness 3.20 mm |
396 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® VAC7041 ABS+PBT+PET (Asia Pacific) |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 395 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6 GF6 UG BK MB 6% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 6% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Heat Stabilized and LubricatedAppearance.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 396 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Thermocomp OB008 PPS - Branched LNP* Thermocomp* OB008 is a compound based on Branched PPS containing Glass Beads.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 396 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP PH0240A PA 6 LNP* THERMOCOMP* PH0240A is a compound based on Nylon 6 resin. Added features of this grade include: High Impact, High Specific Gravity. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C @Thickness 6.40 mm |
396 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL GTX GTX9400W PPE+PS+PA High flow PPO+PA. Power distribution box applications. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C @Thickness 6.40 mm |
396 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL GTX GTX9400W PPE+PS+PA (Asia Pacific) High flow PPO+PA. Power distribution box applications. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C @Thickness 3.20 mm |
396 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-LOY PF306 PA 6 LNP* STAT-LOY* PF306 is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added feature of this grade includes: Antistat. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 395 °F | Unannealed; ASTM D648 |
| Techmer ES Plastiblend® ABS/PBT GF20 Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 396 °F | Absolute Drying; ASTM-D648 |
| Toyobo GLAMIDE® NB-5550 Nylon/Olefin GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 396 °F | ASTM D648 |
| E-Polymers Tekaloy® T80GFR , Flame Retardant, 30% Glass Fiber Reinforced PBT/ABS Alloy 30% Glass Fiber reinforced, Flame RetardantInformation provided by E-Polymers Co. Ltd. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 396 °F | |
| Arkema Group Orgalloy® RS 66K15LT Nylon 66 Alloy, Mineral/Impact Grade (Conditioned) RS 66 series, rigid polyamide 66 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional propertie.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 396 °F | ISO 75-2/B |
| Ascend Performance Materials Vydyne® 49 Nylon 66, DAM Vydyne® 49 is a general-purpose, impact-modified PA66 resin. Available in natural, it is recognized for all the processing and property advantages inherent to PA66 with the addition of improved imp.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 396 °F | ASTM D648 |
| Ashley Polymers Ashlene® 520MS/520SMS Nylon 66, MoS2 Filled A general purpose Molybdenum-disulfide filled nylon resin.Data provided by the manufacturer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 396 °F | ASTM D648 |
| A. Schulman ComAlloy Voloy® 462 Glass/Mineral Reinforced, PBT Alloy, Flame Retardant, UL Data provided by the manufacturer, ComAlloy International Company.35% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 396 °F | Unannealed; ISO 75-2/B |
| Ascend Performance Materials Vydyne® 49 Nylon 66, Impact Modified, DAM Vydyne® 49 is general-purpose, impact-modified PA66 resin. Available in natural, is recognized for all the processing and property advantages inherent to PA66 with the addition of improved impact s.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 396 °F | Unannealed; ISO 75-2/B |
| Ascend Performance Materials Vydyne® 49H NT Nylon 66, Impact Modified, DAM Vydyne® 49H NT is general-purpose, impact-modified PA66 resin. Available in natural, it is heat-stabilized for improved resistance to elevated temperatures. The heat-stabilized for improved resista.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 396 °F | ASTM D648 |