- HOME
- POLYMER SEARCH
- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 154 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 154 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648-95 |
| Multibase Multi-Pro® 2010 X Natural 20% Filler Content Polypropylene Data provided by Multibase. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | DIN 53461 |
| Polycasa PETG QUINN PETG has good optical properties and a brilliant surface. The PETG range of sheets are easy to fabricate, to vacuum form, and show exceptional low temperature performance. Important benefits o.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.8 °C | 154 °F | ASTM D648 |
| Ineos B4020N1332 Polyethylene Copolymer This is a unique high density polyethylene copolymer intended for the injection or compression molding of closures for beverages. Because of its high purity and excellent organoleptic properties, t.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648-82 |
| Micropol Microcene MC123 Metallocene Based Polyethylene Rotational Molding Powder Characteristics: reduced fusion, compacting, and crystallization times or lower oven temperatures; improved wall thickness control, improved impact resistance; low warpage; better creep resistance. .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP TH0450A PUR LNP THERMOCOMP* TH0450A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP TH0450A PUR (Asia Pacific) LNP THERMOCOMP* TH0450A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | Unannealed; ASTM Data |
| Styron Magnum™ 347EZ ABS MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 3701 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C @Thickness 3.20 mm |
154 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 392 Ionomer Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C @Thickness 3.20 mm |
154 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 392 Ionomer Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C @Thickness 3.20 mm |
154 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 392 Ionomer Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648 |
| Eastman Cadence™ GS4 Copolyester for film calendering Eastman Cadence™ copolyester, for calendered films, is a specialty plastic developed to meet the demand for an environmentally responsible material for the calendering industry. Available in diffe.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | |
| Eastman Eastapak 9921 PET ISO data as provided by the manufacturer, Eastman Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648 |
| Eastman Eastar GN120 Copolyester Applications:AppliancesConsumer electronicsPersonal care and cosmeticsStationary suppliesKey Attributes:High clarity and transparencyHigh flow copolyesterToughProduct Description: Eastar GN120 Cop.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648 |
| Eastman Tenite 485E3720023 Butyrate Clear, Trsp Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite cellulosi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648 |
| Eastman Tenite Butyrate 485A2R30023 Natural, Trsp Cellulose Acetate Butyrate Plasticizer 23%. Weight loss on heating = 1.2% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648 |
| Eastman Tenite Butyrate 565A3720023 Clear, Trsp Cellulose Acetate Butyrate Plasticizer 23%. Weight loss on heating = 1.2% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® FN718 BK230A Nylon 66
(Unverified Data**) Zytel® FN718 BK230A is a flexible, plasticizer free modified black polyamide 66 resin having good heat aging and chemical resistance.Information provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.8 °C | 154 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
| Dow DMDA-8980 NT 7 High Density Polyethylene Resin DOW DMDA-8980 NT 7 is produced using UNIPOL™ process technology. It is intended for use in thin wall injection molding applications such as food containers. Information provided by Dow |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.8 °C | 154 °F | Unannealed; ASTM D648 |
| Dow DS6D81 Polypropylene Random Copolymer Resin OverviewConsistent processabilityGood optical propertiesLow temperature heat sealComplies with U.S. FDA 21 CFR 177.1520 (c)3.1a, Canadian HPFB No ObjectionDOW DS6D81 Polypropylene Resin is intended .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.8 °C | 154 °F | unannealed; molded and tested in accordance with ASTM D 4101; ASTM D648 |
| Dow DS6D81 Polypropylene Resin DOW DS6D81 is intended for use as a heat seal coating on oriented polypropylene (OPP) film.Information provided by DowDow Announced Sale of Global Polypropylene Business to Braskem in July 2011. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.8 °C | 154 °F | Unannealed; ASTM D648 |
| Dow DS6D82 Polypropylene Random Copolymer Resin OverviewConsistent processabilityGood optical propertiesLow temperature heat sealComplies with U.S. FDA 21 CFR 177.1520 (c)3.1aDOW DS6D82 Polypropylene Resin is intended for use as a heat seal coati.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM-D648 |
| Braskem GM5240PR HDPE High Density Extrusion Polyethylene GM5240PR is a high-density polyethylene compound specially developed for the manufacturing of pipes, underground conduits, and steel pipe coating. This resin is produced with bimodal technology and .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM-D648 |
| Braskem GM7040G HDPE High Density Extrusion Polyethylene GM7040G is a high-density polyethylene compound specially developed for the manufacturing of extruded pipes for a gas pressurized line. It is produced with bimodal technology and has high molar mass.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.8 °C | 154 °F | ASTM D648 |
| Aclo Accutech Polypropylene Copolymer CP0437C10L1 Calcium Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM-D648 |
| Braskem IH57 HDPE Injection Molding Polyethylene Copolymer IH57 is a high-density polyethylene, narrow molecular weight butene-1 copolymer produced by the solution process for injection molding applications. It offers high stress cracking resistance with pr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | |
| Covestro Texin® 970U Urethane Thermoplastic Elastomer Key Features:UnfilledU.V. stabilized or stable to weatherSuitable processing methods:Injection moldingProfile extrusionSheet extrusionInformation provided by Bayer Polymers.As of 1 September 2015, B.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C @Thickness 3.20 mm |
154 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 392 Ionomer Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 - 95.0 °C | 154 - 203 °F | Average value: 81.7 °C Grade Count:41 |
| Overview of materials for Cellulose Acetate Butyrate, Molded This property data is a summary of similar materials in the MatWeb database for the category "Cellulose Acetate Butyrate, Molded". Each property range of values reported is minimum and maximum value.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648 |
| ExxonMobil Paxon™ AA50-002 Blow Molding Resin
(discontinued **) AA50-002 is a blow molding grade high density polyethylene. This resin has excellent stress crack resistance combined with high impact strength, rigidity, and melt strength.Information provided by .. |
|||