Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 145 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 63.0 °C
145 °F
ASTM D648
Mytex Polymers AN18KW-01 FK Polypropylene, Rubber modified
Description: Rubber modified polypropylene produced for automotive interior applications using Mytex® Technology. Specifically designed to achieve ductile performance at cold temperatures during a..
Deflection Temperature at 0.46 MPa (66 psi) 63.0 - 67.0 °C
145 - 153 °F
ASTM D648-06
Proto3000 Objet RGD525 High Temperature Prototyping Polymer
Information provided by Proto3000 for their protoyping engineering services.
Deflection Temperature at 0.46 MPa (66 psi) 63.0 °C
145 °F
ASTM D648
LyondellBasell Adsylâ„¢ 5C30F Thermoplastic Olefin Resin
Primary Processing Method: Film extrusionKey Features: thermoplastic olefin resins for film extrusion, good clarity and gloss, good moisture barrier properties, very low seal initiation temperature,..
Deflection Temperature at 0.46 MPa (66 psi) 63.0 °C
145 °F
ASTM D648
LyondellBasell Adsylâ„¢ 5C37F Thermoplastic Olefin Resin
Primary Processing Method: Film extrusionKey Features: thermoplastic olefin resins for film extrusion, good clarity and gloss, good moisture barrier properties, very low seal initiation temperature,..
Deflection Temperature at 0.46 MPa (66 psi) 63.0 °C
145 °F
ISO 75
LyondellBasell Hifaxâ„¢ CA45 Thermoplastic Olefin Resin
Key Features: medium melt flow, medium modulus thermoplastic elastomeric olefin resin, excellent balance of properties, excellent processability, good colorability, excellent surface appearanceAppli..
Deflection Temperature at 0.46 MPa (66 psi) 62.8 °C
145 °F
Unannealed; ASTM D648
Techmer ES HiFill® HDPE TM20 20% Talc Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Talc Filler, 20% Filler by WeightInformation provided by TP Composites, Inc.
Deflection Temperature at 0.46 MPa (66 psi) 62.8 °C
145 °F
Unannealed; ASTM D648
Techmer ES HiFill® HDPE TM20 UV BK 20% Talc Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Talc Filler, 20% Filler by WeightAdditive: UV StabilizerFeatures: Good UV ResistanceAppearance: BlackInformation provided by TP Composi..
Deflection Temperature at 0.46 MPa (66 psi) 62.8 °C
145 °F
Unannealed; ASTM D648
Techmer ES HiFill® HDPE TM25 25% Talc Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Talc Filler, 25% Filler by WeightInformation provided by TP Composites, Inc.
Deflection Temperature at 0.46 MPa (66 psi) 62.5 °C
145 °F
Teknor Apex TELCAR® 1000-92 Thermoplastic Elastomer
Information provided by Teknor Apex Company
Deflection Temperature at 0.46 MPa (66 psi) 62.5 °C
145 °F
Teknor Apex TELCAR® 1000-92UV Thermoplastic Elastomer
Information provided by Teknor Apex Company
Deflection Temperature at 0.46 MPa (66 psi) 62.8 °C
145 °F
Unannealed; ASTM D648
Teknor Apex Telcar® TL-1000-92 Thermoplastic Elastomer
Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Automotive Spec..
Deflection Temperature at 0.46 MPa (66 psi) 62.8 °C
145 °F
Unannealed; ASTM D648
Teknor Apex Telcar® TL-1000-92-UV Thermoplastic Elastomer
Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Automotive Spec..
Deflection Temperature at 0.46 MPa (66 psi) 63.0 °C

@Thickness 3.20 mm
145 °F

@Thickness 0.126 in
ISO 75
A. Schulman FORMION™ FI 330 Ionomer
Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 63.0 °C

@Thickness 3.20 mm
145 °F

@Thickness 0.126 in
ISO 75
A. Schulman FORMION™ FI 330 Ionomer
Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 63.0 °C

@Thickness 3.20 mm
145 °F

@Thickness 0.126 in
ISO 75
A. Schulman FORMION™ FI 330 Ionomer
Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 63.0 °C

@Thickness 3.20 mm
145 °F

@Thickness 0.126 in
ISO 75
A. Schulman FORMION™ FI 330 Ionomer
Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 63.0 °C

@Thickness 3.20 mm
145 °F

@Thickness 0.126 in
ISO 75
A. Schulman FORMION™ FI 330 Ionomer
Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 63.0 °C

@Thickness 3.20 mm
145 °F

@Thickness 0.126 in
ISO 75
A. Schulman FORMION™ FI 330 Ionomer
Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 63.0 °C
145 °F
Eastman Ecdel PCCE 9967 Copolyester Ether Elastomer
ISO data as provided by the manufacturer, Eastman Chemical
Deflection Temperature at 0.46 MPa (66 psi) 62.8 °C
145 °F
ASTM D648-98c
DSM Somos® ProtoGen™ 18920 Liquid Photopolymer, UV Postcure at HOC +3
Product DescriptionDSM Somos® ProtoGen 18920 is a liquid photopolymer that produces accurate, ABS-like parts ideal for general purpose applications. ProtoGen resins are the first SL resins to demo..
Deflection Temperature at 0.46 MPa (66 psi) 62.8 °C
145 °F
ASTM D648
Aclo Accucomp Polypropylene CPO407L Copolymer
Deflection Temperature at 0.46 MPa (66 psi) 63.0 - 65.0 °C
145 - 149 °F
C.O.I.M. EXTER S® S 105 Orthophthalic Resin
Description: The Exter S product line contains a large number of unsaturated polyester resin products with an array of properties and applications.Specific Notes for ESTER S® S 105: Medium reactivi..
Deflection Temperature at 0.46 MPa (66 psi) 63.0 °C
145 °F
ASTM D648
ACC EP QSZ EPI Engineered Polymers Quick Set Epoxy with Zinc
EP QSZ Quick Set Epoxy with Zinc, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC’s (Volatile Organic Compound), self-leveling modified epoxy. This versatile new gene..
Deflection Temperature at 0.46 MPa (66 psi) 63.0 °C
145 °F
ASTM D648
ACC EP QS EPI Engineered Polymers Quick Set Epoxy
EP QS Quick Set Epoxy, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC, self-leveling modified epoxy. This versatile new generation epoxy displays low blush, fast cure..
Deflection Temperature at 0.46 MPa (66 psi) 63.0 °C
145 °F
ISO 75-2
Borealis Borsoft™ SG220MO Polypropylene Random Copolymer for Injection Molding
Borsoft™ SG220MO is a polypropylene characterized by good flow, high impact and good transparency. This grade contains antistatic and demolding additives which, together with enhanced nucleation, ..
Deflection Temperature at 0.46 MPa (66 psi) 63.0 °C
145 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP LUBRICOMP FP003 PE (Europe-Africa-Middle East)
LNP *Lubricomp* FP003 is a compound based on Polyethylene resin, containing PTFE and Silicone. Added features include: Internally Lubricated.