Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 16.5 µm/m-°C @Temperature 200 °C |
9.17 µin/in-°F @Temperature 392 °F |
|
Outokumpu 4306 Cr-Ni Austenitic Stainless Steel General purpose steel with good corrosion resistance.Applications: Wide variety of applications in construction, chemical, petroleum, automobile, and domestic appliance markets.Available in hot roll.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 20.0 - 200 °C |
9.17 µin/in-°F @Temperature 68.0 - 392 °F |
|
Industeel CLC 17.12.2 L 2% Mo Containing 18 Cr –10 Ni Austenitic Stainless Steel Description: CLC 17-12-2L is one of the basic grade of the stainless steels range. 2% Molybdenum bearing ensures better corrosion resistance than CLC 18-9 L grade, particularly regarding to uniform .. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 20.0 - 200 °C |
9.17 µin/in-°F @Temperature 68.0 - 392 °F |
|
Industeel CLC 18.10 LN Nitrogen Containing 18Cr-10Ni Austenitic Stainless Steel Description: CLC 18.10LN is a 18Cr-10Ni austenitic stainless steel with specific Nitrogen additions. Its low carbon content avoids intergranular corrosion, even on welded pieces without an ulterior .. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 20.0 - 200 °C |
9.17 µin/in-°F @Temperature 68.0 - 392 °F |
|
Industeel CLC 18.10Ti Titanium-Stabilized 18Cr-10Ni Austenitic Stainless Steel CLC 18-10Ti is a 18Cr-9Ni austenitic stainless steel stabilized with some Titanium additions. This is a basic grades in the stainless steel range. Titanium bearing (carbide forming element) avoids i.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 20.0 - 500 °C |
9.17 µin/in-°F @Temperature 68.0 - 932 °F |
|
Industeel URANUS® B66 High Strength Super-Austenitic Stainless Steel with PREN = 54 Description: Research carried out these last five years has shown that combined additions of chromium, tungsten, molybdenum, nitrogen and copper, make it possible to design a super-austenitic stainl.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, hot rolled and 1175°C solution annealed plate Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, plate at RT after 16000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 25 alloy, cold rolled and 1205°C (2200°F) solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 25 alloy, cold worked sheet, 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 25 alloy, room temperature sheet after 1000 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 100 °C |
9.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
ATI Allegheny Ludlum Stainless Steel Chromium-Nickel-Molybdenum 317L (UNS S31703) Allegheny Ludlum's 317L™ is molybdenum-bearing austenitic stainless steel with greatly increased resistance to chemical attack as compared to the conventional chromium-nickel austenitic stainless s.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 20.0 - 93.0 °C |
9.17 µin/in-°F @Temperature 68.0 - 199 °F |
|
ATI Allegheny Ludlum Altemp® A286 Iron-Base Superalloy, UNS S66286 Allegheny Ludlum Altemp A286 alloy is an iron-base superalloy useful for applications requiring high strength and corrosion resistance up to 704 degrees Celsius and for lower stress applications at .. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 21.1 - 816 °C |
9.17 µin/in-°F @Temperature 70.0 - 1500 °F |
|
Kennametal Stellite Stellite® 31 PM after P/M processing, aged 8 hours at 802°C air cooled Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous we.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 20.0 - 300 °C |
9.17 µin/in-°F @Temperature 68.0 - 572 °F |
|
Industeel UREA 25.22.2 Plants Description: CLI UREA 25.22.2 chemical composition has been optimized for specific uses in Urea plants. It is a 310L modified austenitic stainless steel with low carbon, low silicon and high nitroge.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |