- Polymer Property : CTE, linear = 8.61 µin/in-°F
Polymer Property : CTE, linear = 8.61 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.5 µm/m-°C @Temperature 30.0 - 538 °C |
8.61 µin/in-°F @Temperature 86.0 - 1000 °F |
|
| Haynes Hastelloy® G-30® alloy, all-weld metal, GTAW weld 3.2 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 30.0 - 538 °C |
8.61 µin/in-°F @Temperature 86.0 - 1000 °F |
|
| Haynes Hastelloy® G-30® alloy, mill annealed HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged at 649°C (1200°F) for 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 25.0 - 600 °C |
8.61 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes HR-160® alloy, plate, aged 1000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 30.0 - 538 °C |
8.61 µin/in-°F @Temperature 86.0 - 1000 °F |
|
| Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GMAW spray weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 30.0 - 538 °C |
8.61 µin/in-°F @Temperature 86.0 - 1000 °F |
|
| Haynes Hastelloy® G-30® alloy, 25.4 mm thick bar HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 30.0 - 538 °C |
8.61 µin/in-°F @Temperature 86.0 - 1000 °F |
|
| Haynes Hastelloy® G-30® alloy, 3.2 mm thick sheet HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 30.0 - 538 °C |
8.61 µin/in-°F @Temperature 86.0 - 1000 °F |
|
| Haynes Hastelloy® G-30® alloy, 30% cold rolled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 30.0 - 538 °C |
8.61 µin/in-°F @Temperature 86.0 - 1000 °F |
|
| Haynes Hastelloy® G-30® alloy, 50% cold rolled and 1 hour at 500°C, air cooled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 30.0 - 538 °C |
8.61 µin/in-°F @Temperature 86.0 - 1000 °F |
|
| Haynes Hastelloy® G-30® alloy, 50% cold rolled and 5000 hours at 500°C, air cooled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 30.0 - 538 °C |
8.61 µin/in-°F @Temperature 86.0 - 1000 °F |
|
| Haynes Hastelloy® G-30® alloy, plate and bar HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 25.0 - 600 °C |
8.61 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes HR-160® alloy plate, aged 8000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 200 °C |
8.61 µin/in-°F @Temperature 68.0 - 392 °F |
|
| ATI Allegheny Ludlum Stainless Steel AL-6XN® Alloy (UNS N08367), 30% Cold Work The AL-6XN® alloy is a superaustenitic stainless steel which was developed by Allegheny Ludlum Corporation. It exhibits far greater resistance to chloride pitting, crevice corrosion and stress-co.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 200 °C |
8.61 µin/in-°F @Temperature 68.0 - 392 °F |
|
| ATI Allegheny Ludlum Stainless Steel AL-6XN® Alloy (UNS N08367), 50% Cold Work The AL-6XN® alloy is a superaustenitic stainless steel which was developed by Allegheny Ludlum Corporation. It exhibits far greater resistance to chloride pitting, crevice corrosion and stress-co.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 30.0 - 538 °C |
8.61 µin/in-°F @Temperature 86.0 - 1000 °F |
|
| Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW short arc weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 30.0 - 538 °C |
8.61 µin/in-°F @Temperature 86.0 - 1000 °F |
|
| Haynes Hastelloy® G-30® alloy, 31.8 mm thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| CTE, linear | 15.5 µm/m-°C @Temperature 30.0 - 538 °C |
8.61 µin/in-°F @Temperature 86.0 - 1000 °F |
|
| Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||