Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 14.1 µm/m-°C @Temperature 21.0 - 316 °C |
7.83 µin/in-°F @Temperature 69.8 - 601 °F |
|
Kennametal Stellite Stellite® 31 PM cast Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous we.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 0.000 - 200 °C |
7.83 µin/in-°F @Temperature 32.0 - 392 °F |
|
Kennametal Stellite Stellite® 6 PM with P/M Processing Adhesive wear test data: 0.49 P/M, 0.48 Cast; Typical applications include: (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) die.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 0.000 - 200 °C |
7.83 µin/in-°F @Temperature 32.0 - 392 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 1.6 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 0.000 - 200 °C |
7.83 µin/in-°F @Temperature 32.0 - 392 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 12.7 mm (1/2 in.) thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 0.000 - 200 °C |
7.83 µin/in-°F @Temperature 32.0 - 392 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.0 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 0.000 - 200 °C |
7.83 µin/in-°F @Temperature 32.0 - 392 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.7 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 0.000 - 200 °C |
7.83 µin/in-°F @Temperature 32.0 - 392 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 0.000 - 200 °C |
7.83 µin/in-°F @Temperature 32.0 - 392 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 15.9 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 0.000 - 200 °C |
7.83 µin/in-°F @Temperature 32.0 - 392 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 15.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 0.000 - 200 °C |
7.83 µin/in-°F @Temperature 32.0 - 392 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 4.8 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 0.000 - 200 °C |
7.83 µin/in-°F @Temperature 32.0 - 392 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 20.0 - 1000 °C |
7.83 µin/in-°F @Temperature 68.0 - 1830 °F |
|
Kennametal Stellite Stellite® 98M2 with P/M Processing Adhesive wear test data P/M 0.58 Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy sheet Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, 10% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, 20% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, 20% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, 20% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, 20% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, 30% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, 30% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, 40% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, 40% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, sheet, 100 hours exposure at 980°C (1800°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, sheet, 1000 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, sheet, 32 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, 30% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 21.0 - 500 °C |
7.83 µin/in-°F @Temperature 69.8 - 932 °F |
Mean |
Special Metals INCONEL® 725 Nickel Superalloy (UNS N07725), Annealed Round Tensile strength (ultimate and yield), hardness, and elongation values reported here are typical for Annealed Round samples. Other property values are typical of INCONEL® alloy 725.Data provided.. |