- Polymer Property : CTE, linear = 7.06 µin/in-°F
Polymer Property : CTE, linear = 7.06 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.7 µm/m-°C @Temperature 20.0 - 600 °C |
7.06 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| Kennametal Stellite Nucalloy® 488V High-Silicon Nickel-Base Hardfacing Alloy Applications include diesel engine valves, and injection mold screws.Nucalloy® alloys are unique, patented, high-silicon, nickel-base hardfacing alloys that are designed to have optimum combinati.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 230® alloy, 0% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 230® alloy, 10% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 230® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 230® alloy, 20% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 600 °C |
7.06 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Bar, Hot Rolled and Solution Annealed HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 21.0 - 427 °C |
7.06 µin/in-°F @Temperature 69.8 - 801 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 538°C (1000°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 21.0 - 427 °C |
7.06 µin/in-°F @Temperature 69.8 - 801 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 704°C (1300°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 21.0 - 427 °C |
7.06 µin/in-°F @Temperature 69.8 - 801 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, welded and tested as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 21.0 - 427 °C |
7.06 µin/in-°F @Temperature 69.8 - 801 °F |
|
| Haynes Hastelloy® N, weld metal, aged 500 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 230® alloy, plate, 8000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 300 °C |
7.06 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 263® alloy, cold rolled sheet, solution treated and aged Very good aged strength properties, excellent fabrication characteristics when annealed, excellent intermediate temperature tensile ductility, is not normally subject to strain age cracking, excelle.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.06 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes Hastelloy® C-22HS™ Nickel Alloy Gas Tungsten Arc Welded (GTAW) All Weld Cruciform Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.06 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes Hastelloy® C-22HS™ Nickel Alloy Plate, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.06 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes Hastelloy® C-22HS™ Nickel Alloy Plate, Annealed Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.06 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes Hastelloy® C-22HS™ Nickel Alloy Sheet, Cold-rolled, Solution Annealed Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.06 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes Hastelloy® C-22HS™ Nickel Alloy Sheet, Cold-rolled, Solution Annealed, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.06 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes Hastelloy® C-22HS™ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 500 °C |
7.06 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 600 °C |
7.06 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 600 °C |
7.06 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Sheet, Cold Rolled and Solution Annealed HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 600 °C |
7.06 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 230® alloy, plate, 16000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.06 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes Hastelloy® C-22HS™ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately doubl.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 500 °C |
7.06 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Plate, Hot Rolled and Solution Annealed HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing spe.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 600 °C |
7.06 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing spe.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 21.0 - 427 °C |
7.06 µin/in-°F @Temperature 69.8 - 801 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 593°C (1100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 230® alloy plate, 8000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||