- Polymer Property : CTE, linear = 14.3 µm/m-°C
Polymer Property : CTE, linear = 14.3 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, cold worked sheet, 20 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, hot rolled and 1230°C solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, cold rolled and 1205°C (2200°F) solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, cold worked sheet, 15 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, room temperature after 25% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, room temperature after 25% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, room temperature after 25% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, room temperature sheet after 100 hours of 760°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, room temperature sheet after 100 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, room temperature sheet after 1000 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, room temperature sheet after 2500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, vacuum investment castings, solution treated Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| HP Alloys Alloy 718, 20% Cold Worked 20% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internati.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| HP Alloys Alloy 718, 25% Cold Worked, Aged 25% Cold Worked, Aged applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Int.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| HP Alloys Alloy 718, 30% Cold Worked, Aged 30% Cold Worked, Aged applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Int.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, room temperature after 0% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, room temperature after 20% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| HP Alloys Alloy 718, 10% Cold Worked, Aged 10% Cold Worked, Aged applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Int.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| HP Alloys Alloy 718, 5% Cold Worked, Aged 5% Cold Worked, Aged applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Inte.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 100 °C |
7.94 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Latrobe MP159® Alloy MP159 is an alloy of the Multiphase family of alloys possessing the unique combination of ultra-high strength, ductility and corrosion resistance. Through work strengthening and aging, MP159 alloy .. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||