Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 13.6 µm/m-°C @Temperature 0.000 - 800 °C |
7.56 µin/in-°F @Temperature 32.0 - 1470 °F |
|
Kennametal Stellite Stellite® STAR with P/M Processing Applications: Vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, wear pads, pins, balls, hardfa.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 0% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 10% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 20% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 20% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 30% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 40% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 40% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, 50% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, cold rolled annealed sheet 2.0-3.2 mm thick Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, sheet, 100 hours exposure at 870°C (1600°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 214® alloy, sheet, 1000 hours exposure at 870°C (1600°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, cold worked sheet, 20 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 21.0 - 500 °C |
7.56 µin/in-°F @Temperature 69.8 - 932 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2025°F (1107°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, room temperature after 25% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, room temperature sheet after 100 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, room temperature sheet after 1000 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, room temperature sheet after 500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 21.0 - 500 °C |
7.56 µin/in-°F @Temperature 69.8 - 932 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 20.0 - 1000 °C |
7.56 µin/in-°F @Temperature 68.0 - 1830 °F |
|
ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™ (ASTM XM-8; UNS S43035) Allegheny Ludlum Stainless Steel Type 439, a titanium stabilized, 18 percent chromium alloy, also known as ASTM XM-8 and by the UNS designation S43035, is a ferritic stainless steel designed to resi.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 20.0 - 1000 °C |
7.56 µin/in-°F @Temperature 68.0 - 1830 °F |
|
ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™, 30% cold work (ASTM XM-8; UNS S43035) Allegheny Ludlum Stainless Steel Type 439, a titanium stabilized, 18 percent chromium alloy, also known as ASTM XM-8 and by the UNS designation S43035, is a ferritic stainless steel designed to resi.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, room temperature after 10% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 25.0 - 300 °C |
7.56 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 25 alloy, room temperature after 20% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 21.0 - 500 °C |
7.56 µin/in-°F @Temperature 69.8 - 932 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Sheet, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 20.0 - 1000 °C |
7.56 µin/in-°F @Temperature 68.0 - 1830 °F |
|
ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™, 50% cold work (ASTM XM-8; UNS S43035) Allegheny Ludlum Stainless Steel Type 439, a titanium stabilized, 18 percent chromium alloy, also known as ASTM XM-8 and by the UNS designation S43035, is a ferritic stainless steel designed to resi.. |
|||
CTE, linear | 13.6 µm/m-°C @Temperature 20.0 - 430 °C |
7.56 µin/in-°F @Temperature 68.0 - 806 °F |
|
Haynes 617 Nickel Alloy Plate Haynes 617 alloy is a nickel-chromium-cobalt-molybdenum alloy with a good combination of metallurgical stability, strength, and oxidation resistance at high temperatures. The alloy is readily formed.. |