Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 12.2 µm/m-°C @Temperature 204 °C |
6.80 µin/in-°F @Temperature 400 °F |
x-ply; 8HS form; ASTM D696 |
Park Electrochemical Nelcote® F-555 Phenolic Prepreg, ENKA Reinforced Nelcote® F-555 is a carbon-filled MIL-R-9299 phenolic resin optimized for coating Carbonized Rayon cloth. F-555 is used extensively in the manufacture of high temperature rocket nozzles, heat shiel.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 300 °C |
6.78 µin/in-°F @Temperature 68.0 - 572 °F |
|
Kennametal Stellite Nucalloy® 488 High-Silicon Nickel-Base Hardfacing Alloy Nucalloy® alloys are unique, patented, high-silicon, nickel-base hardfacing alloys that are designed to have optimum combinations of hardness and toughness, similar to the cobalt base alloys . B.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 500 °C |
6.78 µin/in-°F @Temperature 68.0 - 932 °F |
|
International Mold Steel Daido DRM1 Matrix High-Speed Steel This tough matrix type high speed tool steel features high hardness and high tough Matrix type high speed tool steel vastly surpasses hot work die steels. DRM1 improves hot and warm die life by its .. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
Haynes Hastelloy® S alloy, weld metal, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
Haynes Hastelloy® S alloy, weld metal, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 500 °C |
6.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 242® alloy, after 4000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 500 °C |
6.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 700 °C |
6.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
Haynes Hastelloy® B-3® alloy, 0% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 700 °C |
6.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
Haynes Hastelloy® B-3® alloy, 30% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 700 °C |
6.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
Haynes Hastelloy® B-3® alloy, 40% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 700 °C |
6.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
Haynes Hastelloy® B-3® alloy, 50% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 300 °C |
6.78 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Sheet, Cold Rolled and Solution Annealed HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 300 °C |
6.78 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 21.1 - 427 °C |
6.80 µin/in-°F @Temperature 70.0 - 800 °F |
|
Crucible Steel CPM® Nu-Die® EZ Tool Steel CRUCIBLE CPM Nu-Die EZ is a new, patented die and mold steel designed for service as die casting dies and plastic injection molds. It is supplied in the prehardened condition, and is easily machined.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 21.1 - 593 °C |
6.79 µin/in-°F @Temperature 70.0 - 1100 °F |
|
Crucible Steel CSM® S60V (440V) Tool Steel, AISI 440C Modified CPM S60V is a unique tool steel made by the Crucible Particle Metallurgy process. It is designed from a 440C stainless base analysis with added high carbon and vanadium for exceptionally good wear r.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 200 °C |
6.80 µin/in-°F @Temperature 68.0 - 392 °F |
low temp. tempering, hardened to 62 HRC |
Bohler-Uddeholm AISI D2 Cold Work Tool Steel AISI D2 is a high-carbon, high-chromium tool steel alloyed with molybdenum and vanadiumAISI AD2 is characterized by: High wear resistance High compressive strength Good through-hardening properties.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 399 °C |
6.80 µin/in-°F @Temperature 750 °F |
hardened to 46 HRC |
Bohler-Uddeholm UDDEHOLM CORRAX® Precipitation Hardening Stainless Mold Steel A precipitation hardening stainless steel which offers excellent high corrosion resistance, excellent dimensional stability during hardening and good wear resistance. It can be used at its as-suppli.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature <=427 °C |
6.78 µin/in-°F @Temperature <=801 °F |
|
AK Steel 15-5 PH® Precipitation Hardening Stainless Steel, Condition H 1075 AK Steel 15-5 PH® provides high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), and good toughness in both base metal and welds. Short-time, .. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature <=427 °C |
6.78 µin/in-°F @Temperature <=801 °F |
|
AK Steel 17-4 PH® Precipitation Hardening Stainless Steel, Condition H 1075 AK Steel 17-4 PH® provides an outstanding combination of high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), and good toughness in both base.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 21.0 - 649 °C |
6.78 µin/in-°F @Temperature 69.8 - 1200 °F |
|
Carpenter Micro-Melt® 9 Hardened and Tempered Tool Steel Micro-Melt® 9 tool steel is a high vanadium tool steel produced using the Carpenter Micro-Melt powder process. This grade possesses wear resistance superior to most other tool steels along with goo.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 400 °C |
6.78 µin/in-°F @Temperature 68.0 - 752 °F |
|
Carpenter No. 610® High Carbon, High Chrome Tool Steel (Air-Wear) (AISI D2) No. 610 tool steel is an air hardening, high-carbon, high-chromium tool steel having extremely high wear resisting properties. It is very deep hardening, and will be practically free from size chang.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 300 °C |
6.78 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing spe.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 21.1 - 93.3 °C |
6.80 µin/in-°F @Temperature 70.0 - 200 °F |
|
Schmolz + Bickenbach Cryodur® 2312 (Brake Die) Cold Work Die Steel Description: Cryodur® 2312 is a pre-hardened single melt Extra Fine Structure (EFS) plastic mold steel and Re-sulphurized to improve machinabilityCharacteristics: Excellent machinability compared t.. |
|||
CTE, linear | 12.2 µm/m-°C @Temperature 21.1 - 93.3 °C |
6.80 µin/in-°F @Temperature 70.0 - 200 °F |
|
Schmolz + Bickenbach Formadur® 2311 Plastic Mold Steel Description: Formadur® 2311 is a pre-hardened plastic mold steelCharacteristics: Good texturing compared to Formadur®2312 and Good polishability compared to Formadur® 231Applications: Injection m.. |