Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Transverse to Flow | 84.0 - 120 µm/m-°C | 46.7 - 66.7 µin/in-°F | Average value: 103 µm/m-°C Grade Count:14 |
Overview of materials for Polybutylene Terephthalate (PBT), Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Flame Retardant". Each property range of values reported is minimum an.. |
|||
CTE, linear, Transverse to Flow | 80.0 - 120 µm/m-°C | 44.4 - 66.7 µin/in-°F | Average value: 96.0 µm/m-°C Grade Count:5 |
Overview of materials for Acetal Copolymer, 10% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, 10% Glass Fiber Reinforced". Specific grades with glass content between 5% and 14% ar.. |
|||
CTE, linear, Transverse to Flow | 80.0 - 120 µm/m-°C | 44.4 - 66.7 µin/in-°F | Average value: 98.8 µm/m-°C Grade Count:8 |
Overview of materials for Acetal Copolymer, Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Mineral Filled". Each property range of values reported is minimum and maximum values .. |
|||
CTE, linear, Transverse to Flow | 90.0 - 120 µm/m-°C | 50.0 - 66.7 µin/in-°F | Average value: 107 µm/m-°C Grade Count:49 |
Overview of materials for Acetal Homopolymer, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Homopolymer, Unreinforced". Each property range of values reported is minimum and maximum values .. |
|||
CTE, linear, Transverse to Flow | 75.0 - 120 µm/m-°C | 41.7 - 66.7 µin/in-°F | Average value: 97.0 µm/m-°C Grade Count:4 |
Overview of materials for Nylon 66/Nylon 6 Blend, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/Nylon 6 Blend, Glass Fiber Filled". Each property range of values reported is minimum and maxim.. |
|||
CTE, linear, Transverse to Flow | 70.0 - 120 µm/m-°C | 38.9 - 66.7 µin/in-°F | Average value: 97.2 µm/m-°C Grade Count:18 |
Overview of materials for Nylon 12, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. .. |
|||
CTE, linear, Transverse to Flow | 60.0 - 120 µm/m-°C @Temperature 23.0 - 80.0 °C |
33.3 - 66.7 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
BASF Ultramid® C3U PA66/6 (Dry) Ultramid C3U is an injection molding, general purpose PA66/6 grade with improved flame retardance. |
|||
CTE, linear, Transverse to Flow | 80.0 - 120 µm/m-°C @Temperature 23.0 - 55.0 °C |
44.4 - 66.7 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1/-2 |
BASF Ultramid® Seal-Fit PA6/66 (Dry) Description: Transparent, tough, amorphous copolyamide for injection molding, specially developed for tight overmoulding of metal inlays.Information provided by BASF |
|||
CTE, linear, Transverse to Flow | 40.0 - 120 µm/m-°C | 22.2 - 66.7 µin/in-°F | Average value: 80.8 µm/m-°C Grade Count:4 |
Overview of materials for Polyethylene Terephthalate (PET), 20% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 20% Glass Reinforced". Specific grades with glass content between 15% .. |