Polymer Property : CTE, linear, Transverse to Flow = 41.4 µm/m-°C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
CTE, linear, Transverse to Flow 41.4 µm/m-°C

@Temperature -20.0 - 150 °C
 23.0 µin/in-°F

@Temperature -4.00 - 302 °F
 ASTM E831
Polymer Resources PEI-G30 Polyetherimide, 30% Glass Reinforced
Polyetherimide, 30% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Poly..
CTE, linear, Transverse to Flow 41.4 µm/m-°C

@Temperature -20.0 - 150 °C
 23.0 µin/in-°F

@Temperature -4.00 - 302 °F
 ASTM E 831
SABIC Innovative Plastics ULTEM 2310 PEI
30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.
CTE, linear, Transverse to Flow 41.4 µm/m-°C

@Temperature -20.0 - 150 °C
 23.0 µin/in-°F

@Temperature -4.00 - 302 °F
 ASTM E 831
SABIC Innovative Plastics ULTEM 2310 PEI (Asia Pacific)
30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.
CTE, linear, Transverse to Flow 41.4 µm/m-°C

@Temperature -20.0 - 150 °C
 23.0 µin/in-°F

@Temperature -4.00 - 302 °F
 ASTM E 831
SABIC Innovative Plastics ULTEM 2310R PEI
30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
CTE, linear, Transverse to Flow 41.4 µm/m-°C

@Temperature -20.0 - 150 °C
 23.0 µin/in-°F

@Temperature -4.00 - 302 °F
 ASTM E 831
SABIC Innovative Plastics ULTEM 2310R PEI (Asia Pacific)
30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
CTE, linear, Transverse to Flow 41.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 23.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
SABIC Innovative Plastics LNP STAT-KON DX04489C PC
LNP STAT-KON* DX04489C is a high modulus compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Con..
CTE, linear, Transverse to Flow 41.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 23.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
SABIC Innovative Plastics LNP Thermocomp OB008 PPS - Branched
LNP* Thermocomp* OB008 is a compound based on Branched PPS containing Glass Beads.This data was supplied by SABIC-IP for the Americas region.