Polymer Property : CTE, linear, Transverse to Flow = 18.9 µin/in-°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
CTE, linear, Transverse to Flow	34.0 - 62.0 µm/m-°C @Temperature 55.0 - 260 °C	18.9 - 34.4 µin/in-°F @Temperature 131 - 500 °F	Average value: 47.7 µm/m-°C Grade Count:3
Overview of materials for Liquid Crystal Polymer (LCP), Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), Mineral Filled". Each property range of values reported is minimum and max..
CTE, linear, Transverse to Flow	34.0 - 62.0 µm/m-°C @Thickness 2.00 - 4.00 mm	18.9 - 34.4 µin/in-°F @Thickness 0.0787 - 0.157 in	Average value: 47.7 µm/m-°C Grade Count:3
Overview of materials for Liquid Crystal Polymer (LCP), Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), Mineral Filled". Each property range of values reported is minimum and max..
CTE, linear, Transverse to Flow	34.0 - 2980 µm/m-°C	18.9 - 1660 µin/in-°F	Average value: 473 µm/m-°C Grade Count:7
Overview of materials for Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler". Specific grades with glass content between 25%..
CTE, linear, Transverse to Flow	34.0 - 100 µm/m-°C	18.9 - 55.6 µin/in-°F	Average value: 66.3 µm/m-°C Grade Count:24
Overview of materials for Nylon 6, Glass/Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass/Mineral Reinforced". Each property range of values reported is minimum and maximum values..
CTE, linear, Transverse to Flow	34.0 Âµm/m-Â°C @Temperature -30.0 - 30.0 Â°C	18.9 Âµin/in-Â°F @Temperature -22.0 - 86.0 Â°F	ASTM D696
SABIC Innovative Plastics LNP LUBRICOMP UX06427 PPA LNP* LUBRICOMP* UX06427 is a compound based on PPA containing 30% Carbon Fiber, 15% PTFE. Added features of this grade include: Heat Stabilized, Hot Water Moldable, Wear Resistant.
CTE, linear, Transverse to Flow	34.0 µm/m-°C @Temperature 20.0 °C	18.9 µin/in-°F @Temperature 68.0 °F
Covestro Baygal® 90 IK 20 Polyurethane Uses: Suitable for the production of parts: for example: insulators, bushing insulators, components of switchgear cabinets.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience..
CTE, linear, Transverse to Flow	34.0 µm/m-°C	18.9 µin/in-°F	dry; ISO 11359-1/-2
DSM Stanyl® TW200B6 PA46-CF30 30% Carbon Reinforced, Heat Stabilized, Lubricated
CTE, linear, Transverse to Flow	34.0 µm/m-°C @Temperature 23.0 - 150 °C	18.9 µin/in-°F @Temperature 73.4 - 302 °F	ASTM E 228
DuPont Performance Polymers VESPEL TP-8541 Polyimide Thermoplastic parts from filled PI (polyimide) for high mechanical properties and impact performance in high temperature environmentsInformation provided by DuPont Performance Polymers
CTE, linear, Transverse to Flow	34.0 µm/m-°C @Temperature 50.0 - 150 °C	18.9 µin/in-°F @Temperature 122 - 302 °F	z direction; IPC TM-650 2.4.24
Arlon CLTE Microwave Printed Circuit Board Substrate CLTE is a ceramic powder-filled and woven micro fiberglass reinforced PTFE composite engineered to produce a stable, low water absorption laminate with a nominal Dielectric Constant of 2.98.Ceramic/..
CTE, linear, Transverse to Flow	34.0 - 38.0 µm/m-°C @Temperature 23.0 - 80.0 °C	18.9 - 21.1 µin/in-°F @Temperature 73.4 - 176 °F	DIN 11359-1/-2
BASF Ultramid® B3WGM 24 HP BK 23210 10/20% Glass/Mineral Filled PA6-1 (Dry) Description: 20% mineral-filled and 10% glass-fiber reinforced injection-molding grade with outstanding flowability for technical parts with medium rigidity and high dimensional stability, e.g. for..
CTE, linear, Transverse to Flow	34.0 - 110 µm/m-°C	18.9 - 61.1 µin/in-°F	Average value: 62.4 µm/m-°C Grade Count:3
Overview of materials for Acetal Copolymer, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, PTFE Filled". Each property range of values reported is minimum and maximum values of ..
CTE, linear, Transverse to Flow	34.0 - 76.0 µm/m-°C	18.9 - 42.2 µin/in-°F	Average value: 51.7 µm/m-°C Grade Count:3
Overview of materials for Polycarbonate, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, PTFE Filled". Each property range of values reported is minimum and maximum values of app..
CTE, linear, Transverse to Flow	34.0 µm/m-°C @Temperature 20.0 °C	18.9 µin/in-°F @Temperature 68.0 °F	TMA; ASTM E831
LNP Lubricomp® JFL-4036 Polyethersulfone, Glass Fiber Reinforcement, PTFE Lubricant (discontinued **) Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still ac..
CTE, linear, Transverse to Flow	34.0 µm/m-°C @Thickness 1.60 mm	18.9 µin/in-°F @Thickness 0.0630 in	ASTM D696
E-Polymers SEPAZ® K130HF 30% Glass Fiber Reinforced High Flow PPS Resin Polyphenylene Sulfide Resin: High-performance engineering plastic SEPAZ PPS boasts excellent high-temperature resistance, flame retardancy and chemical resistance, physical strength, and its fluidit..
CTE, linear, Transverse to Flow	34.0 - 42.0 µm/m-°C	18.9 - 23.3 µin/in-°F	Average value: 38.7 µm/m-°C Grade Count:3
Overview of materials for Thermoset Polyurethane, Liquid, Quartz Filled This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Polyurethane, Liquid, Quartz Filled". Each property range of values reported is minimum and ma..