Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 187 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 86.0 °C

@Thickness 3.20 mm
187 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics Lexan® JK2000 PC+ABS (Asia Pacific)
Lexan* JK2000 compound is a glass reinforced, non-Br and non-Cl FR polycarbonate blends designed for thinwall molding applications.
Deflection Temperature at 1.8 MPa (264 psi) 86.1 °C

@Thickness 3.18 mm
187 °F

@Thickness 0.125 in
Annealed; ASTM D648
PolyOne Geon™ HTX Ultra LA426 Tan 3725 Polyvinyl Chloride Alloy (PVC Alloy)
Optimum for Black and Darker Colors between 50 and 70 L value. Also suitable for colors above 70 L value.Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Physical propert..
Deflection Temperature at 1.8 MPa (264 psi) 86.1 °C

@Thickness 3.18 mm
187 °F

@Thickness 0.125 in
Annealed; ASTM D648
PolyOne Geon™ HTX Ultra LA426G Black 2880 Polyvinyl Chloride Alloy (PVC Alloy)
Higher gloss version of Geon HTX Ultra LA426Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Physical properties measured on LA426G Black 2880.Information provided by Pol..
Deflection Temperature at 1.8 MPa (264 psi) 86.1 °C

@Thickness 3.18 mm
187 °F

@Thickness 0.125 in
Unannealed; ASTM D648
PolyOne Geon™ HTX Ultra LA427Plus Polyvinyl Chloride Alloy (PVC Alloy)
Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Physical properties based on Geon HTX Ultra LA427Plus Natural 0000Information provided by PolyOne
Deflection Temperature at 1.8 MPa (264 psi) 86.0 °C

@Thickness 6.40 mm
187 °F

@Thickness 0.252 in
Unannealed; ASTM D648
LG Chemical HF380U ABS, High Flow
Feature: Injection Molding, High Flow, Good WeatherabilityApplication: Electric & Electronic Products, Miscellaneous Goods)CAS No. 9003-56-9Information provided by LG Chemical
Deflection Temperature at 1.8 MPa (264 psi) 86.0 °C

@Thickness 6.40 mm
187 °F

@Thickness 0.252 in
Unannealed; ASTM D648
LG Chemical HI100H ABS, High Impact, High Toughness
Feature: Injection Molding, High Impact, High ToughnessApplication: Helmet, Pipe & Fittings)CAS No. 9003-56-9Information provided by LG Chemical
Deflection Temperature at 1.8 MPa (264 psi) 86.0 °C

@Thickness 6.40 mm
187 °F

@Thickness 0.252 in
Unannealed; ASTM D648
LG Chemical HI121H ABS, High Stiffness
Feature: Injection Molding, High StiffnessApplication: Electric & Electronic Products, Miscellaneous GoodsCAS No. 9003-56-9Information provided by LG Chemical
Deflection Temperature at 1.8 MPa (264 psi) 86.0 °C

@Thickness 12.7 mm
187 °F

@Thickness 0.500 in
Unannealed; ASTM-D648
Ineos ABS Lustran® ABS 248FC Medical & Food Contact Grade
Lustran® ABS 248FC resin is a high-gloss, medium-impact grade of ABS (acrylonitrile butadiene styrene). This injection molding grade offers a good balance of physical properties and has been desi..
Deflection Temperature at 1.8 MPa (264 psi) 86.0 °C

@Thickness 6.40 mm
187 °F

@Thickness 0.252 in
Unannealed; ASTM D648
LG Chemical PT270 ABS
Feature: Injection Molding, Good PaintabilityApplication: Exterior Part of Automobile and Motor cycleCAS No. 9003-56-9Information provided by LG Chemical
Deflection Temperature at 1.8 MPa (264 psi) 86.0 °C

@Thickness 6.40 mm
187 °F

@Thickness 0.252 in
unannealed; ASTM D 648
SABIC Innovative Plastics Noryl PX6021 PPE+PS (Asia Pacific)
Low heat, flame retardant PPO/HIPS alloy.This data was supplied by SABIC-IP for the Asia Pacific region.
Deflection Temperature at 1.8 MPa (264 psi) 86.0 °C

@Thickness 3.20 mm
187 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP Lexan_JK2000 PC+ABS
LNP* Thermocomp* Lexan_JK2000 compound is a 22% GR, ECO-compliant FR, PC+ABS for thinwall molding applications.