Polymer Property : CTE, linear, Parallel to Flow = 11.1 µin/in-°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	10.0 - 20.0 µm/m-°C @Temperature 50.0 - 100 °C	5.56 - 11.1 µin/in-°F @Temperature 122 - 212 °F	ISO 11359-2
Raschig Group 2557 AMC Polyester Glass fiber reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, exceptional processability with short cycle time and low ..
CTE, linear, Parallel to Flow	15.0 - 20.0 µm/m-°C @Temperature 50.0 - 150 °C	8.33 - 11.1 µin/in-°F @Temperature 122 - 302 °F	ISO 11359-2
Raschig Group DECAL® 572R Phenolic Glass-fiber reinforced phenolic molding compound. Exceptional heat resistance with regard to maintaining surface finish and mechanical properties, outstanding mechanical properties, excellent rotati..
CTE, linear, Parallel to Flow	15.0 - 20.0 µm/m-°C @Temperature 50.0 - 150 °C	8.33 - 11.1 µin/in-°F @Temperature 122 - 302 °F	ISO 11359-2
Raschig Group EN 5004 Epoxy Molding Compound Mica reinforced molding compound. Low mold shrinkage and post-shrinkage, very good electrical values, outstanding heat resistance, very goo pourablity. This product meets the allowed upper limits fo..
CTE, linear, Parallel to Flow	15.0 - 20.0 µm/m-°C @Temperature 50.0 - 150 °C	8.33 - 11.1 µin/in-°F @Temperature 122 - 302 °F	ISO 11359-2
Raschig Group EN 5007 Epoxy Molding Compound Mica reinforced molding compound. Low mold shrinkage and post-shrinkage, very good electrical values, outstanding heat resistance, very goo pourablity. This product meets the allowed upper limits fo..
CTE, linear, Parallel to Flow	15.0 - 20.0 µm/m-°C @Temperature 50.0 - 150 °C	8.33 - 11.1 µin/in-°F @Temperature 122 - 302 °F	ISO 11359-2
Raschig Group EPOXIDUR® 3580 EP Epoxy Glass-fiber reinforced and mineral filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties even with thin wall thicknesses and high temperatures. This prod..
CTE, linear, Parallel to Flow	15.0 - 20.0 µm/m-°C @Temperature 50.0 - 150 °C	8.33 - 11.1 µin/in-°F @Temperature 122 - 302 °F	ISO 11359-2
Raschig Group EPOXIDUR® 3581 T-1 EP Epoxy, Molded, Glass Fiber Filler Glass-fiber reinforced and inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. Very ..
CTE, linear, Parallel to Flow	15.0 - 20.0 µm/m-°C @Temperature 50.0 - 150 °C	8.33 - 11.1 µin/in-°F @Temperature 122 - 302 °F	ISO 11359-2
Raschig Group EPOXIDUR® 3585 EP Epoxy, Molded, Glass Fiber Filler Glass-fiber reinforced and inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures, excel..
CTE, linear, Parallel to Flow	10.0 - 20.0 µm/m-°C @Temperature 50.0 - 100 °C	5.56 - 11.1 µin/in-°F @Temperature 122 - 212 °F	ISO 11359-2
Raschig Group RALUPOL® 4566 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability. This product meets the allowed u..
CTE, linear, Parallel to Flow	10.0 - 20.0 µm/m-°C @Temperature 50.0 - 100 °C	5.56 - 11.1 µin/in-°F @Temperature 122 - 212 °F	ISO 11359-2
Raschig Group RALUPOL® 4802 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability. This product meets the allowed u..
CTE, linear, Parallel to Flow	10.0 - 20.0 µm/m-°C @Temperature 50.0 - 100 °C	5.56 - 11.1 µin/in-°F @Temperature 122 - 212 °F	ISO 11359-2
Raschig Group RALUPOL® 5000 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very good electrical values, excellent heat resistance, good mechanical strength. This product meets the all..
CTE, linear, Parallel to Flow	10.0 - 20.0 µm/m-°C @Temperature 50.0 - 100 °C	5.56 - 11.1 µin/in-°F @Temperature 122 - 212 °F	ISO 11359-2
Raschig Group RALUPOL® 802 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength, good heat resistance. This product meets the allowed up..
CTE, linear, Parallel to Flow	10.0 - 20.0 µm/m-°C @Temperature 50.0 - 100 °C	5.56 - 11.1 µin/in-°F @Temperature 122 - 212 °F	ISO 11359-2
Raschig Group RALUPOL® 804 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy m..
CTE, linear, Parallel to Flow	15.0 - 20.0 µm/m-°C @Temperature 50.0 - 150 °C	8.33 - 11.1 µin/in-°F @Temperature 122 - 302 °F	ISO 11359-2
Raschig Group RESINOL® 87120 EPF Phenolic Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and very good mechanical properties. This product meets ..
CTE, linear, Parallel to Flow	10.0 - 20.0 µm/m-°C @Temperature 50.0 - 100 °C	5.56 - 11.1 µin/in-°F @Temperature 122 - 212 °F	ISO 11359-2
Raschig Group SURAPLAST 54 UPA Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for..
CTE, linear, Parallel to Flow	10.0 - 20.0 µm/m-°C @Temperature 50.0 - 100 °C	5.56 - 11.1 µin/in-°F @Temperature 122 - 212 °F	ISO 11359-2
Raschig Group SURAPLAST UPA 63 UP Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for..
CTE, linear, Parallel to Flow	5.00 - 20.0 µm/m-°C @Temperature 23.0 - 80.0 °C	2.78 - 11.1 µin/in-°F @Temperature 73.4 - 176 °F	DIN 11359-1/-2
BASF Ultramid® A3EG10 50% Glass Filled PA66 (Dry) Description: 50% glass-fiber reinforced injection-molding grade for technical articles of very high stiffness as well as for electric insulating parts.Information provided by BASF
CTE, linear, Parallel to Flow	15.0 - 20.0 µm/m-°C @Temperature 23.0 - 80.0 °C	8.33 - 11.1 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-1/-2
BASF Ultramid® B3EG7 35% Glass Filled PA6 (Dry) Description: 35% Glass fiber reinforced injection molding grade for industrial articles and electrical insulating parts.Information provided by BASF
CTE, linear, Parallel to Flow	15.0 - 20.0 µm/m-°C @Temperature 23.0 - 80.0 °C	8.33 - 11.1 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-1/-2
BASF Ultramid® B3EG7 BK 00564 35% Glass Filled PA6 (Dry) Description: 35% Glass fiber reinforced injection molding grade for industrial articles and electrical insulating parts.Information provided by BASF
CTE, linear, Parallel to Flow	10.0 - 20.0 µm/m-°C @Temperature 23.0 - 80.0 °C	5.56 - 11.1 µin/in-°F @Temperature 73.4 - 176 °F	DIN 11359-1/-2
BASF Ultramid® B3ZG8 BK 20560 40% Glass Filled PA6-1 (Dry) Description: Impact-modified and 40% glass-fiber reinforced injection-molding grade for technical articles of very high stiffness and toughness, for instance, for vehicle airbag housings and suitcas..
CTE, linear, Parallel to Flow	15.0 - 20.0 µm/m-°C @Temperature 23.0 - 80.0 °C	8.33 - 11.1 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-1/-2
BASF Ultramid® A3EG7 35% Glass Filled PA66 (Dry) Ultramid A3EG6 is a 35% glass fiber reinforced injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability.
CTE, linear, Parallel to Flow	15.0 - 20.0 µm/m-°C @Temperature 23.0 - 80.0 °C	8.33 - 11.1 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-1/-2
BASF Ultramid® A3X2G7 35% Glass Filled PA66 (Dry) Ultramid A3X2G7 is a 35% glass fiber reinforced injection molding PA66 grade with improved flame retardance and enhanced long-term stability. Flame retardant based on red phosphorus; very high stif..
CTE, linear, Parallel to Flow	15.0 - 20.0 µm/m-°C @Temperature 23.0 - 80.0 °C	8.33 - 11.1 µin/in-°F @Temperature 73.4 - 176 °F	DIN 11359-1/-2
BASF Ultramid® B3WG7 BK 00564 30% Glass Filled PA6 (Dry) Description: 35% glass-fiber reinforced and heat aging resistant injection-molding grade, e.g. for automotive manifolds and pedals.Information provided by BASF
CTE, linear, Parallel to Flow	10.0 - 20.0 µm/m-°C @Temperature 50.0 - 100 °C	5.56 - 11.1 µin/in-°F @Temperature 122 - 212 °F	ISO 11359-2
Raschig Group RALUPOL® 8605 UP Polyester Glass fiber reinforced polyester molding compound. Resistant to hydrolysis. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU dire..
CTE, linear, Parallel to Flow	15.0 - 20.0 µm/m-°C @Temperature 50.0 - 150 °C	8.33 - 11.1 µin/in-°F @Temperature 122 - 302 °F	ISO 11359-2
Raschig Group RESINOL® 400 EPF Phenolic Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and very good mechanical properties. This product meets ..