Polymer Property : Crystallization Temperature = 144 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Crystallization Temperature	144 °C	291 °F	DSC, both heating and cooling speeds of 20°C/min
Noltex Soarnol® A4412 Ethylene Vinyl Alcohol Copolymer Ethylene content 44 mol%. Volatile matter 0.3%.The gas barrier property of Soarnol is about forty times better than that of nylon, therefore, Soarnol allows design of lower cost packages by using a..
Crystallization Temperature	144 °C	291 °F	DSC, both heating and cooling speeds of 20°C/min
Noltex Soarnol® AT4403 Ethylene Vinyl Alcohol Copolymer High ethylene content, low melting point. Suitable for use in multilayer structures where ease of thermoforming is required. Ethylene content 44 mol%.The gas barrier property of Soarnol is about fo..
Crystallization Temperature	144 - 163 °C	291 - 325 °F	Average value: 156 °C Grade Count:13
Overview of materials for Ethylene Vinyl Alcohol (EVOH) This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Vinyl Alcohol". Each property range of values reported is minimum and maximum values of appropr..
Crystallization Temperature	144 - 148 Â°C	291 - 298 Â°F	Peak; ASTM D3418
Solvay Specialty Polymers SolefÂ® 60512/0550 and 60512/0150 Polyvinylidene Fluoride (PVDF) SolefÂ® 60512/0550 and SolefÂ® 60512/0150 are PVDF grades compounded with PTFE for extrusion of anti-wear tapes.Features: CopolymerUses: TapeAdditional Properties: Crystallization Heat - ASTM D3..
Crystallization Temperature	144 °C	291 °F
Addcomp PRIEX® 11002 Maleic Anhydride Grafted HDPE Uses: Enhance sealability in bi-oriented polypropylene film packagingIncrease adhesion between metallic or textile wire and polymer coatingAchieve high compatibility between glass or other natural f..
Crystallization Temperature	144 °C	291 °F
Addcomp PRIEX® 11006 Maleic Anhydride Grafted HDPE Uses: Enhance sealability in bi-oriented polypropylene film packagingIncrease adhesion between metallic or textile wire and polymer coatingAchieve high compatibility between glass or other natural f..