Polymer Property : Shear Strength = 8.96 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Shear Strength	>= 8.96 MPa @Temperature 149 °C	>= 1300 psi @Temperature 300 °F	Tensile lap, Al to Al
Master Bond EP46HT Epoxy Adhesive for Structural Bonding Description: Master Bond System EP46HT is a newly formulated two component high performance heat resistant epoxy resin system with excellent mechanical strength and chemically resistant properties f..
Shear Strength	8.96 MPa @Temperature 82.2 °C	1300 psi @Temperature 180 °F	Cure cycle: 7 days @ RT , with Aced Etched 6061-T6 Aluminum
Zyvex Performance Materials Epovex™ Nano-Engineered Composite Epoxy Adhesive Paste Epovex® Adhesive Paste is a carbon nanotube enhanced two part epoxy adhesive thixotropic paste. Used for bonding or filling, Epovex Paste is ideal for many metals, woods, masonry products, and some..
Shear Strength	8.96 MPa @Temperature 93.3 °C	1300 psi @Temperature 200 °F	Lap Shear
Hexcel® Redux® 335K Adhesive film for bonding metallic and composite components (0.03 psf) Redux 335 is a film adhesive curing at 250F. It is available in a range of standard areal weights from 0.015 to 0.06 psf. It is available either unsupported or with knitted and/or matt carrier for a..
Shear Strength	8.96 MPa @Temperature 25.0 °C	1300 psi @Temperature 77.0 °F	Tensile, Al/Al lap joint; cured 90 days @ 25°C
Abatron AboCast 8110-4/AboCure 8110-3 Flexible Epoxy This epoxy system can achieve flexibility and plasticity without sacrificing adhesive, electrical, structural, and other properties. This compound is a clear (unfilled) basic formulation. Its applic..
Shear Strength	8.96 MPa @Temperature 0.000 °C	1300 psi @Temperature 32.0 °F	Tensile, Al/Al lap joint; cured 7 days @ 25°C
Abatron AboCast 8110-2/AboCure 8110-3 Flexible Epoxy This epoxy system can achieve flexibility and plasticity without sacrificing adhesive, electrical, structural, and other properties. This compound is a clear (unfilled) basic formulation. Its applic..
Shear Strength	8.96 MPa @Temperature 24.0 °C	1300 psi @Temperature 75.2 °F	Overlap, Plexiglass
3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength	8.96 MPa @Temperature 24.0 °C	1300 psi @Temperature 75.2 °F	Overlap, Plexiglass
3M Scotch-Weld™ 3535 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength	8.96 MPa @Temperature 24.0 °C	1300 psi @Temperature 75.2 °F	Overlap, Plexiglass
3M Scotch-Weld™ 3549 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..