Polymer Property : Shear Strength = 41.4 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Shear Strength	41.4 MPa @Temperature 21.1 °C	6000 psi @Temperature 70.0 °F	Short-Beam, Dry; ASTM D2344
Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 285 Kevlar® Reinforced Nelcote® E-761 is a versatile self-adhesive epoxy matrix for use in aerospace and commercial application where ease of processing and cost are key considerations.Key Features and Benefits:Controlle..
Shear Strength	41.4 MPa @Temperature 71.1 °C	6000 psi @Temperature 160 °F	Short-Beam, Wet; ASTM D2344
Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 7781 E-Glass Reinforced Nelcote® E-761 is a versatile self-adhesive epoxy matrix for use in aerospace and commercial application where ease of processing and cost are key considerations.Key Features and Benefits:Controlle..
Shear Strength	41.4 MPa @Temperature 177 °C	6000 psi @Temperature 351 °F	Short Beam
Hexcel® HexPly® 954-2A Curing Cyanate Resin, S-2 Glass Fiber Reinforced 8 Harness Satin Fabric Information provided by HexCel
Shear Strength	41.4 MPa @Temperature 21.1 °C	6000 psi @Temperature 70.0 °F	Lap Shear
Hexcel® Redux® 312L Modified epoxy film adhesive Redux® 312 is a high-strength 250°F curing film adhesive, suitable for metal to metal bonding and sandwich constructions, where operating temperatures of up to 210°F may be experienced. A support..
Shear Strength	41.4 MPa @Temperature 21.1 °C	6000 psi @Temperature 70.0 °F	Single Lap Shear (Metal/Metal), 0.05 psf, No conditioning
Hexcel® Redux® 330K Epoxy film adhesives for the bonding and finishing of composites Redux 330 is a 350°F curing tough film adhesive which is ideally suited to structural bonding, composite to composite bonding, surface finishing, electromagnetic shielding and lightning strike appl..
Shear Strength	41.4 MPa @Temperature 21.1 °C	6000 psi @Temperature 70.0 °F	Lap Shear
Hexcel® Redux® 335M Adhesive film for bonding metallic and composite components (0.06 psf) Redux 335 is a film adhesive curing at 250F. It is available in a range of standard areal weights from 0.015 to 0.06 psf. It is available either unsupported or with knitted and/or matt carrier for a..