Polymer Property : Shear Strength = 305 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Shear Strength	2.10 MPa @Temperature 82.0 °C	305 psi @Temperature 180 °F	ASTM D1002-64
3M Scotch-Weld™ 3532 B/A Brown Two-Part Urethane Adhesive 3532 B/A Brown (discontinued **) Two-part urethane adhesives cure at room temperature or with heat to provide tough, impact resistant bonds with high peel strength. Features include fast cure adhesive, 20-30 minutes handling stren..
Shear Strength	2.10 MPa @Temperature 82.0 °C	305 psi @Temperature 180 °F	ASTM D1002-64
3M Scotch-Weld™ 3535 B/A Off-white Two-Part Urethane Adhesive 3535 B/A Off-white (discontinued **) Two-part urethane adhesives cure at room temperature or with heat to provide tough, impact resistant bonds with high peel strength. Features include fast cure adhesive, 15-20 minutes handling stren..
Shear Strength	2.10 MPa @Temperature 82.0 °C	305 psi @Temperature 180 °F	ASTM D1002-64
3M Scotch-Weld™ 3549 B/A Brown Two-Part Urethane Adhesive 3549 B/A Brown (discontinued **) Two-part urethane adhesives cure at room temperature or with heat to provide tough, impact resistant bonds with high peel strength. Features include long worklife adhesive, 2-4 hours handling stren..
Shear Strength	2.10 MPa @Temperature 24.0 °C	305 psi @Temperature 75.2 °F	1/8" Birch/High-Pressure Laminate, aged 6 mo
3M Fastbond™ 30-NF Contact Adhesive 3M Fastbond™ Contact Adhesive 30-NF and 30H-NF are water-dispersed, sprayable contact adhesives for high immediate bond strength n long bonding range.Information provided by 3M
Shear Strength	2.10 MPa @Temperature 24.0 °C	305 psi @Temperature 75.2 °F	1/8" Birch/High-Pressure Laminate, aged 6 mo
3M Fastbond™ 30H-NF Contact Adhesive 3M Fastbond™ Contact Adhesive 30-NF and 30H-NF are water-dispersed, sprayable contact adhesives for high immediate bond strength n long bonding range.Information provided by 3M