Polymer Property : Shear Strength = 3000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Shear Strength 20.7 MPa

@Temperature 177 °C
3000 psi

@Temperature 350 °F
Short-Beam, Dry, Autoclave; ASTM D2344
Park Electrochemical Nelcote® E-746 Epoxy Prepreg, 7781 E-Glass Reinforced
Nelcote® E-746 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-746 has a proven history in many demanding aerospac..
Shear Strength 20.7 MPa

@Temperature 37.8 °C
3000 psi

@Temperature 100 °F
ASTM D732
Greene Tweed Avalon® 1 PTFE
Products made from Avalon® thermoplastics are constructed from proprietary high-performance reinforced PTFE material. Greene, Tweeds Avalon thermoplastics, available in grades ranging from virgin..
Shear Strength 20.7 MPa

@Temperature 26.7 °C
3000 psi

@Temperature 80.0 °F
ASTM D732
Greene Tweed Avalon® 7 PTFE, Pigmented and Molybdenum Filled
Products made from Avalon® thermoplastics are constructed from proprietary high-performance reinforced PTFE material. Greene, Tweeds Avalon thermoplastics, available in grades ranging from virgin..
Shear Strength 20.68 MPa

@Temperature 177 °C
3000 psi

@Temperature 350 °F
90 min @ 350°F, Spring Clamp Pressure, FPL Acid Etched 6061-T6; ASTM D1002
Zyvex Performance Materials Aroply™ 350 Nano-Engineered Composite Film Adhesive
Aroply™ 350 Film Adhesive is a versatile, heat curing carbon-nanotube modified epoxy structural film adhesive available in a variety of film weights on a supported carrier. Cured adhesive character..
Shear Strength 20.7 MPa

@Temperature 71.1 °C
3000 psi

@Temperature 160 °F
Tensile Shear, Redux 775 film
Hexcel® Redux® 775 Vinyl phenolic structural adhesive
Redux 775 was adopted as the world's first metal-to-metal bonding process to be officially approved for use in the manufacture of aircraft primary structures in 1943. It is available either as a fil..
Shear Strength 20.7 MPa

@Temperature 24.0 °C
3000 psi

@Temperature 75.2 °F
Overlap
3M Scotch-Weld™ 1838 B/A Green Two-Part Structural Adhesive
Multi-purpose and Rigid bondsInformation provided by 3M
Shear Strength 20.7 MPa

@Temperature -55.0 °C
3000 psi

@Temperature -67.0 °F
Overlap
3M Scotch-Weld™ 2086 One-Part Epoxy Adhesives and Metal Primer
High Temperature strength and High ViscosityInformation provided by 3M
Shear Strength 20.7 MPa

@Temperature -53.0 °C
3000 psi

@Temperature -63.4 °F
Aluminum Overlap
3M Scotch-Weld™ 2214 Hi-Dense Epoxy Adhesive
3M™ Scotch-Weld™ Adhesive 2214 Hi-Dense is a deareted version of Scotch-Weld adhesive 2214 regular for use where a very dense, void free bondline is required. One part 250°F (121°C) curing 100% ..
Shear Strength 20.7 MPa

@Temperature 82.0 °C
3000 psi

@Temperature 180 °F
Aluminum Overlap
3M Scotch-Weld™ 2214 Hi-Temp Epoxy Adhesive
3M™ Scotch-Weld™ Adhesive 2214 Hi-Temp is an aluminum filled, deaerated products fro use where higher strengths are required between 82-177°C. One part 250°F (121°C) curing 100% solids, 3M™ Sc..
Shear Strength 20.7 MPa

@Temperature -55.0 °C
3000 psi

@Temperature -67.0 °F
Overlap
3M Scotch-Weld™ EC2216 Structural Adhesive
High Performance, Very flexible bondsInformation provided by 3M
Shear Strength 20.7 MPa

@Temperature 65.0 °C,
Time 3600 sec
3000 psi

@Temperature 149 °F,
Time 1.00 hour
Lap, Alum to Alum
Atom Adhesives AA-BOND F112 Epoxy Adhesive
AA-BOND F112 is an impact resistant, fiber-optic adhesive. AA-BOND F112 is two-part, low viscosity epoxy has the distinct advantage of remaining below 3000 cps for a minimum of 40 minutes. AA-BOND F..
Shear Strength 20.7 MPa

@Temperature 65.0 °C,
Time 14400 sec
3000 psi

@Temperature 149 °F,
Time 4.00 hour
Lap, Alum to Alum
Atom Adhesives AA-BOND F110 Epoxy Adhesive
AA-BOND F110 is a rigid, optically clear adhesive with a very low viscosity. AA-BOND F110 is room temperature system an excellent choice for thin bond-line assembly and repair applications of prisms..
Shear Strength 20.7 MPa

@Temperature -55.0 °C
3000 psi

@Temperature -67.0 °F
Overlap
3M Scotch-Weld™ 1386 One-Part Epoxy Adhesives and Metal Primer
High Temperature strength and Impact resistanceInformation provided by 3M
Shear Strength 20.7 MPa

@Temperature -53.0 °C
3000 psi

@Temperature -63.4 °F
Aluminum Overlap
3M Scotch-Weld™ 2214 Regular Epoxy Adhesive
3M™ Scotch-Weld™ Adhesive 2214 Regular is an aluminum filled general purpose product for use in applications where high strength bonds are needed in a temperature range of -53-121°C.One part 250°..