Mechanical Properties	Metric	English	Comments
Shear Strength	30.3 MPa @Temperature 71.1 °C	4400 psi @Temperature 160 °F	Short-Beam, Wet; ASTM D2344
Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 3K PW Carbon Reinforced Nelcote® E-761 is a versatile self-adhesive epoxy matrix for use in aerospace and commercial application where ease of processing and cost are key considerations.Key Features and Benefits:Controlle..
Shear Strength	30.3 MPa @Temperature 23.9 °C	4400 psi @Temperature 75.0 °F	Short Beam; Dry; 8HS form; ASTM D5379
Park Electrochemical Nelcote® F-555 Phenolic Prepreg, C2 Reinforced Nelcote® F-555 is a carbon-filled MIL-R-9299 phenolic resin optimized for coating Carbonized Rayon cloth. F-555 is used extensively in the manufacture of high temperature rocket nozzles, heat shiel..
Shear Strength	30.3 MPa @Temperature 23.9 °C	4400 psi @Temperature 75.0 °F	Short Beam; Dry; CMC form; ASTM D5379
Park Electrochemical Nelcote® F-555 Phenolic Prepreg, C2 Reinforced Nelcote® F-555 is a carbon-filled MIL-R-9299 phenolic resin optimized for coating Carbonized Rayon cloth. F-555 is used extensively in the manufacture of high temperature rocket nozzles, heat shiel..
Shear Strength	30.3 MPa @Temperature -40.0 °C	4400 psi @Temperature -40.0 °F	Cure cycle: 7 days @ RT, with Aced Etched 6061-T6 Aluminum
Zyvex Performance Materials Epovex™ Nano-Engineered Composite Epoxy Adhesive Liquid Epovex® Adhesive is a carbon nanotube enhanced ambient or elevated temperature cure two-part epoxy adhesive. Used for bonding, laminating, filling or potting, Epovex is ideal for many metals, woods..
Shear Strength	30.3 MPa @Temperature 23.9 °C	4400 psi @Temperature 75.0 °F	Cure cycle: 2 hrs @ 176°F, with Aced Etched 6061-T6 Aluminum
Zyvex Performance Materials Epovex™ Nano-Engineered Composite Epoxy Adhesive Paste Epovex® Adhesive Paste is a carbon nanotube enhanced two part epoxy adhesive thixotropic paste. Used for bonding or filling, Epovex Paste is ideal for many metals, woods, masonry products, and some..
Shear Strength	30.3 MPa @Temperature -40.0 °C	4400 psi @Temperature -40.0 °F	Cure cycle: 7 days @ RT , with Aced Etched 6061-T6 Aluminum
Zyvex Performance Materials Epovex™ Nano-Engineered Composite Epoxy Adhesive Paste Epovex® Adhesive Paste is a carbon nanotube enhanced two part epoxy adhesive thixotropic paste. Used for bonding or filling, Epovex Paste is ideal for many metals, woods, masonry products, and some..
Shear Strength	30.3 MPa @Temperature 0.000 °C	4400 psi @Temperature 32.0 °F	Tensile, Al/Al lap joint; cured 7 days @ 25°C
Abatron AboCast/AboCure 8110-2 Flexible Epoxy This epoxy system can achieve flexibility and plasticity without sacrificing adhesive, electrical, structural, and other properties. This compound is a clear (unfilled) basic formulation. Its applic..