Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 6.90 MPa @Temperature -55.0 °C |
1000 psi @Temperature -67.0 °F |
ASTM D1002-64 |
3M Scotch-Weld™ DP-605NS Off-White Adhesive in Duo-Pak Cartridges
(discontinued **) Features include fast cure adhesive, semi-rigid urethane, 15-20 minutes handling strength, and excellent gap filler and non sag product for wood and plastic. Mix ratio by volume 1:1. Average T-Peel.. |
|||
Shear Strength | >= 6.89 MPa @Temperature 23.9 °C |
>= 1000 psi @Temperature 75.0 °F |
Tensile, Al to Al |
Master Bond EP3HTS Silver Filled, Electrically Conductive Epoxy Description: Master Bond Polymer System EP3HTS is a one component, silver filled, electrically conductive epoxy system featuring high shear strength and good temperature resistance along with a fast.. |
|||
Shear Strength | 6.89 MPa @Temperature -37.0 °C |
1000 psi @Temperature -34.6 °F |
Overlap, 1/8 birch to 1/8 birch, bond tested after aging 3 weeks @ 24°C and 50% RH at a separation rate of 0.2 in/min; ASTM D1002 |
3M Fastbond™ 2000-NF Contact Adhesive with Spray Activator #1 3M Fastbond™ Contact Adhesive 2000-NF with Spray Activator #1 is a water-dispersed, high solid, activated adhesive which provides immediate bonding capabilities and handling strength without forced.. |
|||
Shear Strength | 6.89 MPa @Temperature 23.0 °C |
1000 psi @Temperature 73.4 °F |
Overlap, Polycarbonate |
3M Scotch-Weld™ TS115 HGS Polyurethane Reactive Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as .. |
|||
Shear Strength | 6.89 MPa @Temperature -40.0 °C |
1000 psi @Temperature -40.0 °F |
Overlap, Solvent Wiped Al |
3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
Shear Strength | 6.89 MPa @Temperature -40.0 °C |
1000 psi @Temperature -40.0 °F |
Overlap, Solvent Wiped Steel |
3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
Shear Strength | 6.89 MPa @Temperature 24.0 °C |
1000 psi @Temperature 75.2 °F |
Overlap, Solvent Wiped Al |
3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
Shear Strength | 6.89 MPa @Temperature -40.0 °C |
1000 psi @Temperature -40.0 °F |
Overlap, Solvent Wiped Al |
3M Scotch-Weld™ 3535 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
Shear Strength | 6.89 MPa @Temperature -40.0 °C |
1000 psi @Temperature -40.0 °F |
Overlap, Solvent Wiped Steel |
3M Scotch-Weld™ 3535 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
Shear Strength | 6.89 MPa @Temperature 24.0 °C |
1000 psi @Temperature 75.2 °F |
Overlap, Solvent Wiped Al |
3M Scotch-Weld™ 3535 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
Shear Strength | 6.89 MPa @Temperature -40.0 °C |
1000 psi @Temperature -40.0 °F |
Overlap, Solvent Wiped Al |
3M Scotch-Weld™ 3549 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
Shear Strength | 6.89 MPa @Temperature -40.0 °C |
1000 psi @Temperature -40.0 °F |
Overlap, Solvent Wiped Steel |
3M Scotch-Weld™ 3549 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
Shear Strength | 6.89 MPa @Temperature 24.0 °C |
1000 psi @Temperature 75.2 °F |
Overlap, Solvent Wiped Al |
3M Scotch-Weld™ 3549 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
Shear Strength | >= 6.89 MPa @Temperature 23.9 °C |
>= 1000 psi @Temperature 75.0 °F |
Tensile, Al to Al |
Master Bond EP3HTSMed Silver Filled, Medical Grade Epoxy Description: Master Bond EP3HTSMed is a one component, silver filled, electrically conductive epoxy system featuring high shear strength and good temperature resistance along with a fast cure schedu.. |