Polymer Property : Flexural Strength = 2900 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	20.0 MPa @Temperature 175 °C	2900 psi @Temperature 347 °F	ISO 178
Victrex® PEEK 150G / 151G Polyetheretherketone, Unreinforced Product Description:High performance thermoplastic material, unreinforced Polyetheretherketone (PEEK), semi crystalline, depth filtered granules for injection moulding, easy flow, FDA food contact c..
Flexural Strength	20.0 MPa @Temperature 175 °C	2900 psi @Temperature 347 °F	ISO 178
Victrex® PEEK 150G903 Black Polyetheretherketone, Unreinforced Product Description:High performance thermoplastic material, unreinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding, easy flow, FDA food contact compliant, colou..
Flexural Strength	20.0 MPa @Temperature 175 °C	2900 psi @Temperature 347 °F	ISO 178
Victrex® PEEK 90G Polyetheretherketone, Unreinforced Product Description:High performance thermoplastic material, unreinforced Polyetheretherketone (PEEK), semi crystalline, depth filtered granules for injection moulding, easy flow, FDA food contact c..
Flexural Strength	20.0 MPa @Temperature 275 °C	2900 psi @Temperature 527 °F	ISO 178
Victrex® ST™ STG45 PolyEtherKetoneEtherKetoneKetone, Unreinforced Product Description:High performance thermoplastic material, unreinforced PolyEtherKetoneEtherKetoneKetone (PEKEKK), semi crystalline, depth filtered granules for injection moulding, standard flow, ..
Flexural Strength	20.0 MPa @Strain 3.50 %	2900 psi @Strain 3.50 %	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® B 31 FCS 000000 Nylon 6, Film Grade PA 6, non-reinforced, extrusion, low viscosity, slip agentInformation provided by LANXESS.
Flexural Strength	20.0 MPa @Strain 3.50 %	2900 psi @Strain 3.50 %	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® B 35 F 000000 Nylon 6, Extrusion, Low Viscosity PA 6, non-reinforced, extrusion, low viscosity, no additivesInformation provided by LANXESS.
Flexural Strength	20.0 MPa @Strain 9.50 %	2900 psi @Strain 9.50 %	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® TP 142-011 900116 Nylon 6 PA 6, non-reinforced, extrusion, blow molding, impact modified, heat-aging stabilizedInformation provided by LANXESS.
Flexural Strength	20.0 MPa @Temperature 194 °C	2900 psi @Temperature 381 °F	ASTM D790
BASF Ultramid® 8202 L Intermediate PA6 (Dry) Description: Ultramid 8202 L-Intermediate is an unreinforced, low viscosity, non-lubricated PA6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is avai..
Flexural Strength	20.0 MPa @Temperature 250 °C	2900 psi @Temperature 482 °F	ASTM D790
BASF Ultramid® 8202 L Intermediate PA6 (Dry) Description: Ultramid 8202 L-Intermediate is an unreinforced, low viscosity, non-lubricated PA6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is avai..
Flexural Strength	20.0 MPa @Temperature 90.0 °C	2900 psi @Temperature 194 °F	ASTM D790
BASF Ultramid® 8270 HS BK 102 PA6 (Dry) Description: Ultramid 8270 HS BK-102 is a thermally modified pigmented black, PA6 blow molding compound exhibiting exceptional toughness and melt strength ideally suited for blow molding, profile ex..
Flexural Strength	20.0 MPa @Temperature 90.0 °C	2900 psi @Temperature 194 °F	ASTM D790
BASF Ultramid® 8281 HS GP PA6 (Dry) Description: Ultramid 8281 HS GP is an unreinforced, heat stabilized PA6 rot molding compound. It is available in natural and black and can be painted. It exhibits excellent balance of engineering p..