Mechanical Properties	Metric	English	Comments
Flexural Strength	138 MPa @Temperature 260 °C	20000 psi @Temperature 500 °F	Dry, Autoclave; ASTM D790
Park Electrochemical Nelcote® E-746 Epoxy Prepreg, 7781 E-Glass Reinforced Nelcote® E-746 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-746 has a proven history in many demanding aerospac..
Flexural Strength	138 MPa @Temperature 23.9 °C	20000 psi @Temperature 75.0 °F	Dry; CMC form; ASTM D790
Park Electrochemical Nelcote® F-555 Phenolic Prepreg, C2 Reinforced Nelcote® F-555 is a carbon-filled MIL-R-9299 phenolic resin optimized for coating Carbonized Rayon cloth. F-555 is used extensively in the manufacture of high temperature rocket nozzles, heat shiel..
Flexural Strength	138 MPa @Thickness 6.35 mm	20000 psi @Thickness 0.250 in	CW
Industrial Laminates/Norplex MC603 Paper Base Laminate (discontinued **) Description: MC603 is constructed from electrical grade of kraft paper and a specially modified phenolic resin system, and is designed to be used in tap changers, coil support plates and terminal pa..
Flexural Strength	138 MPa @Thickness 1.57 mm	20000 psi @Thickness 0.0620 in	CW; ASTM D790
Industrial Laminates/Norplex NP193E Synthetic Fabric Description: 17 oz. aramid and "soft glass" fibers are combined to make a fabric that is stronger than pure aramid and less abrasive than glass fabrics. This material is impregnated with a high temp..
Flexural Strength	138 MPa @Thickness 1.57 mm	20000 psi @Thickness 0.0620 in	LW; ASTM D790
Industrial Laminates/Norplex NP319 Cotton Fabric Base Laminate Description: Bleached canvas combined with phenolic resin and graphite lubricant. Better moisture resistance and machining characteristics than NP315.
Flexural Strength	138 MPa @Thickness 1.57 mm	20000 psi @Thickness 0.0620 in	LW; ASTM D790
Industrial Laminates/Norplex NP615 Paper Base Laminate Description: Room temperature punching and shearing grade up to .125" thick. More flexible and lower mechanical properties than NP611. NP615 is produced with high resin content melamine impregnated ..
Flexural Strength	138 MPa @Thickness 1.57 mm	20000 psi @Thickness 0.0620 in	LW; ASTM D790
Industrial Laminates/Norplex NP630 Paper Base Laminate Description: Machining grade with good electrical properties and moisture resistance. Low cold flow with good dimensional stability. Thickness Tested: 0.062", 0.125", and 0.500"
Flexural Strength	138 MPa @Thickness 1.57 mm	20000 psi @Thickness 0.0620 in	CW; ASTM D790
Industrial Laminates/Norplex NP639 Paper Base Laminate Description: Economical paper reinforced laminate developed with capacity to withstand temperatures to 150Â° C without blistering. High compressive strength and low moisture absorption.Thickness T..