Polymer Property : Flexural Strength = 200 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 200 MPa

@Temperature 23.0 °C
29000 psi

@Temperature 73.4 °F
ISO 178
DuPont Performance Polymers Rynite® FR530 BK507 PET  (Unverified Data**)
Rynite® FR530 BK507 is a 30% glass reinforced, flame retardant, modified polyethylene terephthalate resin.Information provided by DuPont Performance Polymers
Flexural Strength 200 MPa

@Temperature 23.0 °C
29000 psi

@Temperature 73.4 °F
ISO 178
Premix Premi-Glas® 1286 Glass Reinforced SMC
Description: Premi-Glas® 1286 is a glass reinforced thermoset sheet molding compound designed for automotive under the hood applications. Key features and benefits: Designed for compression molding..
Flexural Strength 200 MPa

@Thickness 1.57 mm
29000 psi

@Thickness 0.0620 in
LW; ASTM D790
Industrial Laminates/Norplex NP159 Synthetic Fabric  (discontinued **)
Description: Woven aramid fiber fabric combined with high temperature phenolic resin. With a proper post baking procedure, NP159 will withstand continuous operation at 200° C. Material becomes brit..
Flexural Strength 200 MPa

@Thickness 1.57 mm
29000 psi

@Thickness 0.0620 in
LW; ASTM D790
Industrial Laminates/Norplex NP329 Cotton Fabric
Description: Bleached linen with melamine resin system. Provides better arc resistance than NP320E. Also, resistant to ammonia based refrigerants. Hard, durable material should be heated to punch, ..
Flexural Strength 200 MPa

@Thickness 1.57 mm
29000 psi

@Thickness 0.0620 in
LW; ASTM D790
Industrial Laminates/Norplex NP611 Paper Base Laminate
Description: Hot punching general-purpose phenolic grade. Mechanical properties approach those of NP610 with improved electrical properties and moisture resistance.Thickness Tested: 0.062", 0 125" a..
Flexural Strength 200 MPa

@Thickness 1.57 mm
29000 psi

@Thickness 0.0620 in
LW; ASTM D790
Industrial Laminates/Norplex NP660 Paper Base Laminate
Description: Lower cost paper phenolic NEMA Grade XP. Uses natural kraft paper without pigmented cover sheet. Warm to hot punching. UL listed. Thickness Tested: 0.062", 0.125" & 0.500"
Flexural Strength 200 MPa

@Strain 4.50 %
29000 psi

@Strain 4.50 %
ISO 178
Lanxess Durethan® AKV 15 H3.0 000000 Nylon 66, 15% Glass Fibers
PA 66, 15% glass fibers, injection molding, heat-ageing stabilized
Flexural Strength 200 MPa

@Strain 6.00 %
29000 psi

@Strain 6.00 %
cond., 2 mm/min; ISO 178-A
Lanxess Durethan® AKV 30 000000 Nylon 66, Glass Fiber Reinforced
PA 66, 30% glass fibers, injection moldingInformation provided by LANXESS.
Flexural Strength 200 MPa

@Strain 6.00 %
29000 psi

@Strain 6.00 %
cond., 2 mm/min; ISO 178-A
Lanxess Durethan® AKV 35 H2.0 SR1 901510 Nylon 66, Glass Fiber Reinforced
PA 66, 35% glass fibers, injection molding, heat-aging stabilized, improved surface finishInformation provided by LANXESS.
Flexural Strength 200 MPa

@Strain 5.00 %
29000 psi

@Strain 5.00 %
ISO 178
Lanxess Durethan® BKV 15 H3.0 000000 Nylon 6 Copolymer, 15% Glass Fibers
PA 6 Copolymer, 15% glass fibers, injection molding, heat-ageing stabilized
Flexural Strength 200 MPa

@Strain 3.50 %
29000 psi

@Strain 3.50 %
ISO 178
Lanxess Durethan® BKV 230 H3.0 000000 Nylon 6-Copolymer, 30% Glass Fibers
PA 6-Copolymer, 30% glass fibers, injection molding, impact modified, heat-ageing stabilized
Flexural Strength 200 MPa

@Strain 5.00 %
29000 psi

@Strain 5.00 %
cond., 2 mm/min; ISO 178-A
Lanxess Durethan® BKV 40 H2.0 901510 Nylon 6, Glass Fiber Reinforced
PA 6, 40% glass fibers, injection molding, heat-aging stabilizedInformation provided by LANXESS.
Flexural Strength 200 MPa

@Strain 4.50 %
29000 psi

@Strain 4.50 %
ISO 178
Lanxess Durethan® BKV 325 Z H2.0 901510 Nylon 6, 25% Glass Fibers
PA 6, 25% glass fibers, blow molding, impact modified, heat-ageing stabilized
Flexural Strength 200 MPa

@Temperature 23.0 °C
29000 psi

@Temperature 73.4 °F
Absolute Drying; ASTM-D790
Toyobo GLAMIDE® T-402FR Nylon-6
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength 200 MPa

@Temperature -40.0 °C
29000 psi

@Temperature -40.0 °F
Absolute Drying; ASTM-D790
Toyobo GLAMIDE® T-663G15 Nylon-66
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength 200 MPa

@Thickness >=1.50 mm
29000 psi

@Thickness >=0.0591 in
1hr/150°C/measured at 150°C; ISO 178; IEC/EN 60893-2 5.1
Elektro-Isola G-Etronax EP FR4 Epoxy, Glass Fabric Reinforcement, Light Yellow, Sheets
Description: Extremely high mechanical strength at moderate temperature. Very good stability of electrical properties under high humidity. Mechanical, electrical and electronic applications. UL-94 V..
Flexural Strength 200 MPa

@Thickness >=1.50 mm
29000 psi

@Thickness >=0.0591 in
24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1
Elektro-Isola G-Etronax PM 953 Polyester, Glass Mat, Off White, Sheets
Description: Good electrical properties such as high breakdown voltage in air and oil and highest arc resistance and tracking resistance. Self-extinguishing. Low smoke emission, halogen-free. Very m..
Flexural Strength 200 MPa

@Treatment Temp. 20.0 °C,
Time 3600 sec
29000 psi

@Treatment Temp. 68.0 °F,
Time 1.00 hour
ISO 178; IEC/EN 60893-2 5.1
Elektro-Isola G-Etronax PM 953 Polyester, Glass Mat, Off White, Sheets
Description: Good electrical properties such as high breakdown voltage in air and oil and highest arc resistance and tracking resistance. Self-extinguishing. Low smoke emission, halogen-free. Very m..
Flexural Strength 200 MPa

@Temperature 23.0 °C
29000 psi

@Temperature 73.4 °F
50%RH; ISO 178
DuPont Performance Polymers Zytel® HTN FR52G30NHF BK337 Polyphthalamide (PPA)  (Unverified Data**)
Zytel® HTNFR52G30NHF BK337 is a 30% glass reinforced, flame retardant, lubricated high performance polyamide resin with improved flow. It is also a PPA resin and it uses a non-halogenated flame ret..