Polymer Property : Puncture Energy = 20.0 J Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Puncture Energy 20.0 J
14.8 ft-lb
ISO 6603-2
Lanxess Durethan® A 30 H2.0 901510 Nylon 66
PA 66 standard injection molding grade, non-reinforced, very easy release, good heat-ageing resistanceApplication Examples: terminal blocks, cable clips, bobbins, gearwheels
Puncture Energy 20.0 J

@Temperature -30.0 °C
14.8 ft-lb

@Temperature -22.0 °F
ISO 6603-2
Lanxess Durethan® BC 30 000000 Nylon 6
PA 6, injection molding grade, non-reinforced, rapid processing, higher notched impact strength than B 30 S / B 31 SK in dry and conditioned state, impact-modified
Puncture Energy 20.0 J

@Temperature -30.0 °C
14.8 ft-lb

@Temperature -22.0 °F
Conditioned; ISO 6603-2
Lanxess Durethan® BC 30 000000 Nylon 6
PA 6, injection molding grade, non-reinforced, rapid processing, higher notched impact strength than B 30 S / B 31 SK in dry and conditioned state, impact-modified
Puncture Energy 20.0 J

@Load <=309.1 kg,
Temperature 23.0 °C
14.8 ft-lb

@Load <=681.4 lb,
Temperature 73.4 °F
d.a.m.; ISO 6603-2
Lanxess Durethan® BM 240 000000 Nylon 6, Mineral Reinforced
PA 6, injection molding, 40% mineral, isotopic properties, low warpageInformation provided by LANXESS.
Puncture Energy 20.0 J

@Load <=309.1 kg,
Temperature 23.0 °C
14.8 ft-lb

@Load <=681.4 lb,
Temperature 73.4 °F
ISO 6603-2
Lanxess Durethan® BM 240 H3.0 000000 Nylon 6, 40% Mineral
PA 6, 40% mineral, injection molding, heat-ageing stabilized, low tendency to warp, isotopic properties
Puncture Energy 20.0 J
14.8 ft-lb
ISO 6603-2
Covestro Makrolon® 1095 Polycarbonate, 15% Glass Filled
ISO 7391-PC,MR,(,,)-09-9,GF15Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 min15 % Glass fiber reinforcedHigh viscosityEasy releaseInjection molding - Melt temperature 310 - 330 °CExtrusionAvailable ..