Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Puncture Energy | 15.0 J | 11.1 ft-lb | Conditioned; ISO 6603-2 |
Lanxess Durethan® BKV 130 000000 Copolyamide, 30% Glass Fiber CoPA, injection molding grade, 30% glass fibers, elastomer modified, electroplateable, higher notched impact strength and also higher energy absorption under biaxial impact load than BKV 30, even in.. |
|||
Puncture Energy | 15.0 J | 11.1 ft-lb | Conditioned; ISO 6603-2 |
Lanxess Durethan® BKV 130 H3.0 101006 Copolyamide, 30% Glass Fiber CoPA, injection molding grade, 30% glass fibers, elastomer-modified, electroplateable, higher notched impact strength and also higher energy absorption under biaxial impact load than BKV 30 H3.0, ev.. |
|||
Puncture Energy | 15.0 J @Temperature -30.0 °C |
11.1 ft-lb @Temperature -22.0 °F |
ISO 6603-2 |
Lanxess Pocan® B 1300 000000 PBT PBT, non-reinforced, injection molding, extrusion |
|||
Puncture Energy | 15.0 J @Temperature -30.0 °C |
11.1 ft-lb @Temperature -22.0 °F |
ISO 6603-2 |
Covestro Makrolon® 9415 Polycarbonate, 10% Glass Filled ISO 7391-PC,MFR,(,,)-09-9,GF10Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 min10 % Glass fiber reinforcedChlorine- and bromine-free flame retardantUL 94V-0/1.5 mm and 5VA/3.0 mmHigh viscosityEasy rel.. |
|||
Puncture Energy | 15.0 J @Temperature -30.0 °C |
11.1 ft-lb @Temperature -22.0 °F |
ISO 6603-2 |
Covestro Makrolon® 9417 Polycarbonate, 10% Glass Filled ISO 7391-PC,MFLR,(,,)-09-9,GF10Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 min10 % Glass fiber reinforcedChlorine- and bromine-free flame retardantUL 94V-0/1.5 mm and 5VA/3.0 mmHigh viscosityUV stab.. |