Polymer Property : Flexural Modulus = 8.61 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Modulus 8.61 GPa
1250 ksi
ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP DFL36 PC
LNP* LUBRICOMP* DFL36 is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated.
Flexural Modulus 8.61 GPa
1250 ksi
ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP DFL36XXP PC
LNP* Lubricomp* DFL36XXP is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated.
Flexural Modulus 8.61 GPa
1250 ksi
ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP IFL36 PA6.12
LNP LUBRICOMP* IFL36 is a compound based on Nylon 6/12 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant.
Flexural Modulus 8.61 GPa
1250 ksi
ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP QFP36 PA 6/10
LNP LUBRICOMP* QFP36 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added features of this material include: Wesr Resistant.
Flexural Modulus 8.61 GPa
1250 ksi
ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP QFP36 PA 6/10 (Asia Pacific)
LNP LUBRICOMP* QFP36 is a compound based on Nylon 6/10 resin containing Silicone, PTFE, Glass Fiber. Added features of this material include: Internally Lubricated.
Flexural Modulus 8.61 GPa
1250 ksi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem ATX153R PEI+PCE
30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region.
Flexural Modulus 8.61 GPa
1250 ksi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem ATX153R PEI+PCE (Asia Pacific)
30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Modulus 8.61 GPa
1250 ksi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem ATX153R PEI+PCE (Europe-Africa-Middle East)
30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Europe-Africa-Middle East regio..
Flexural Modulus 8.61 GPa
1250 ksi
ASTM D 790
SABIC Innovative Plastics LNP Thermocomp DF0066P PC
LNP THERMOCOMP* DF0066P is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Exceptional Processing.This data was supplied by..